本文選題：碳化硅　切入點：脈沖激光燒蝕法　出處：《硅酸鹽通報》2017年02期 　論文類型：期刊論文

【摘要】：采用脈沖激光燒蝕法,以多晶3C-SiC陶瓷片為靶材,制備了懸浮于去離子水中的非晶SiC納米顆粒。利用透射電子顯微鏡(TEM)、高分辨透射電子顯微鏡(HRTEM)、傅里葉變換紅外吸收光譜(FTIR)、紫外可見吸收光譜(UV-Vis)和光致發(fā)光譜(PL)等測試手段對其形貌、結(jié)構(gòu)和光學(xué)性質(zhì)進行了分析。結(jié)果表明:這些納米顆粒由大量的非晶SiC構(gòu)成,粒徑在8~9 nm,光學(xué)帶隙為3.28 e V;樣品表現(xiàn)出較強的光致發(fā)光,發(fā)光峰位于415 nm處,這主要是由于量子限制效應(yīng)造成的。
[Abstract]:Using pulsed laser ablation method in polycrystalline 3C-SiC ceramic target and amorphous SiC nanoparticles were prepared in deionized water suspension. Using transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), Fu Liye transform infrared spectroscopy (FTIR), ultraviolet visible absorption spectroscopy (UV-Vis) and photoluminescence (PL) measurements on the morphology, structure and optical properties were analyzed. The results show that these nanoparticles composed of amorphous SiC composition, particle size in 8~9 nm, the optical band gap of 3.28 e V; samples showed a strong photoluminescence emission peak at 415. Nm, this is mainly due to the quantum confinement effect caused.

【作者單位】： 宿遷學(xué)院信息工程學(xué)院;南京郵電大學(xué)電子科學(xué)與工程學(xué)院;
【基金】：國家自然科學(xué)基金資助項目(61474096) 江蘇省高校自然科學(xué)基金資助(15KJD140005) 宿遷市科技計劃項目資助(S201511) 江蘇省青藍工程資助 宿遷學(xué)院科研基金項目資助(2015KY10) 江蘇省333工程科研項目資助(BRA2016262)
【分類號】：TQ163.4;TB383.1

【相似文獻】

相關(guān)期刊論文 前10條

1 季雷華;高素蓮;張斌;;量子點的合成、毒理學(xué)及其應(yīng)用[J];環(huán)境化學(xué);2008年05期

2 王富;劉春艷;;發(fā)光碳量子點的合成及應(yīng)用[J];影像科學(xué)與光化學(xué);2011年04期

3 伊魁宇;王猛;邵明云;;量子點作為離子探針的分析應(yīng)用[J];廣州化工;2012年11期

4 羅慧;李曦;方婷婷;劉鵬;;量子點的毒性研究進展[J];材料導(dǎo)報;2013年19期

5 田瑞雪;武玲玲;趙清;胡勝亮;楊金龍;;碳量子點的氨基化及其對發(fā)光性能的影響[J];化工新型材料;2014年01期

6 ;“量子點”晶體將推動部分物理工藝的進步[J];光機電信息;2002年10期

7 徐萬幫;汪勇先;許榮輝;尹端l，

本文編號：1633709