本文選題：電鍍　切入點(diǎn)：無(wú)光鋅　出處：《電鍍與涂飾》2017年08期 　論文類型：期刊論文

【摘要】：采用烷基糖苷為主添加劑進(jìn)行硫酸鹽體系無(wú)光鍍鋅,表征了鍍層的光澤度、結(jié)合力和耐中性鹽霧腐蝕性能。基礎(chǔ)鍍液組成和工藝條件為:ZnSO_4·7H_2O 225g/L,Na_2SO_4 70g/L,Al_2(SO_4)_3 25g/L,溫度(25±5)°C,電流密度2A/dm~2,時(shí)間25min(鍍層厚度8~12μm)。對(duì)比研究了分別采用烷基糖苷和葡萄糖作添加劑時(shí)所得鍍鋅層的外觀和微觀形貌。結(jié)果表明,使用烷基糖苷作添加劑時(shí)所得鋅鍍層外觀均一,結(jié)晶致密,具有良好的基體結(jié)合力和耐蝕性。
[Abstract]:The APG based additives without light zinc sulfate system, characterization of the coating gloss, adhesion and salt spray corrosion resistance. The bath composition and process conditions were: ZnSO_4, 7H_2O 225g/L, Na_2SO_4 70g/L, Al_2 _3 25g/L (SO_4), temperature (25 + 5) ~ C, current density 2A/dm~2 time, 25min (8~12 thickness m). Comparative study of alkyl glucoside and glucose were used as the additive of the coating appearance and morphology. The results show that the use of alkyl glucoside as the additive of the zinc plating uniform appearance and compact crystal, has good adhesion and corrosion resistance of the substrate.

【作者單位】： 中國(guó)航發(fā)北京航空材料研究院;
【分類號(hào)】：TQ423;TQ153.15

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 鄭艷;蒲曉林;白小東;;烷基糖苷發(fā)展現(xiàn)狀及新進(jìn)展[J];日用化學(xué)品科學(xué);2006年05期

2 金玉芹,肖�？�,樸貞順,張德勝,林晶華,楊錦宗,張淑芬;烷基糖苷的市場(chǎng)狀況及合成工藝進(jìn)展[J];精細(xì)化工;1998年05期

3 王海文;殷馨;龍應(yīng)釗;孔愛國(guó);;一步法合成介孔碳材料實(shí)驗(yàn)探討[J];實(shí)驗(yàn)技術(shù)與管理;2014年06期

4 ;[J];;年期

，

本文編號(hào)：1597832