文獻名稱：鋁合金筒段化學銑切工藝研究

    前言：對2219鋁合金筒段的化學銑切工藝進行了研究,以確定化學銑切工藝的最佳配方和工藝控制要點。對NaOH、Na2S、三乙醇胺(TEA)和溶解Al正交試驗的結(jié)果進行了驗證性試驗,確定了對化學銑切表面粗糙度的影響程度依次為:Na2S、溶解Al、TEA、NaOH,化學銑切溶液的最佳配方為:75~150g/LNaOH,6~15g/LNa2S,38.5~42.0g/LTEA,溶解Al32.5~120·0g/L。按該配方對2219鋁合金筒段進行化學銑切,可達到最佳效果:表面粗糙度1.2~1.4μm、化學銑切壁厚公差≤0·12mm、化學銑切輪廓線線偏離≤0·75mm。
    The chemical milling process for 2219 aluminum alloy tube was investigated using orthogonal test and the optimum formula and technology were established. It was found that the effect of various chemicals on the surface roughness of the chemically milled Al[LL] alloy was ranked as Na_2S>dissolved aluminum>triethanolamine (TEA)>NaOH. The optimum composition of the chemical milling solution was suggested as 75~150 g/L NaOH, 6~15 g/L Na_2S, 38.5~42.0 g/L TEA, and 32.5~120.0 g/L dissolved aluminum. It was able t...

文獻名稱 鋁合金筒段化學銑切工藝研究

Article Name
英文(英語)翻譯 Chemical Milling Process for 2219 Aluminum Alloy Tube;

作者 尹茂生; 廖廣其; 文慶杰; 程紅霞;

Author YIN Mao-sheng~1;2;LIAO Guang-qi~1;WEN Qing-jie~2;CHENG Hong-xia~2（1. School of Materials Science and Engineering;Northwestern Polytechnical University;Xi′an 710072;2. Chengdu Aircraft Industrial Company;Chengdu 610092;China）;

作者單位
Author Agencies 西北工業(yè)大學材料學院; 成都飛機工業(yè)公司熱表中心工藝組; 成都飛機工業(yè)公司熱表中心工藝組 陜西西安; 四川成都; 陜西西安;

文獻出處
Article From 中國科學院上海冶金研究所; 材料物理與化學(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 化學銑切; 2219鋁合金; 表面粗糙度;

Keywords chemical milling;aluminum alloy;surface roughness;

化學銑切槽液中Na_2S的分析
鈦離子含量對鈦合金化學銑切的影響
機械加工中的化學銑切
新一代鋁合金化學銑切保護涂料的研制
化學銑切工藝在15-5PH精密機械零件加工中的研究與應(yīng)用
熱塑彈性體鋁合金化學銑切保護涂料的研制
鋁合金的化學銑切加工
LY16鋁合金的化學銑切
GH3044高溫合金化學銑切工藝及其應(yīng)用
無氰四元合金浸鋅液中金屬離子對鋁合金浸鋅的影響

  本文關(guān)鍵詞：鋁合金筒段化學銑切工藝研究，由筆耕文化傳播整理發(fā)布。