【摘要】：選用國產(chǎn)PVA纖維和不同級配的普通砂分別代替進口PVA纖維和標準砂制作SHCC試樣,測試其28d拉伸應力應變關系、抗壓強度及彈性模量。研究表明:不同級配的砂對SHCC拉伸性能的影響較大,但對抗壓強度和彈性模量的影響較小。選用粒徑小于0.6mm的普通砂和國產(chǎn)PVA纖維可以配制延性較好的SHCC,拉伸過程中可觀察到多條細密裂紋。極限拉應變?yōu)?.05%,拉伸強度為3.1MPa。
[Abstract]:The PVA fiber made in China and the ordinary sand with different grades were used to make SHCC samples instead of imported PVA fibers and standard sand, respectively. The tensile stress-strain relationship of the samples was tested at 28 days. The compressive strength and elastic modulus. The results show that the different grade of sand has a great influence on the tensile properties of SHCC. But it has little effect on compressive strength and elastic modulus. SHCC with good ductility can be prepared by using ordinary sand with diameter less than 0.6 mm and PVA fiber made in China. Several fine cracks can be observed during the tensile process. The ultimate tensile strain is 3.05 and the tensile strength is 3.1 MPA.
【作者單位】： 武漢理工大學理學院工程結構與力學系;恒潤集團有限公司;
【基金】：國家高技術研究發(fā)展計劃(2013AA031306) 湖北省自然科學基金(2014CFB866) 河北省百人計劃項目資助 武漢理工大學自主創(chuàng)新研究基金項目(155214008)
【分類號】：TU528
【正文快照】： 0引言 SHCC(Strain Hardening Cement-based Composites)是一種具有高延性、高韌性和多縫開裂特征的纖維增強水泥基復合材料。最早由Victor Li于20世紀90年代采用聚乙烯醇纖維(又稱為維綸纖維或PVA纖維)作為增強材料,基于細觀力學和斷裂力學方法設計的短纖維增強水泥基復合材

【參考文獻】

相關期刊論文 前6條

1 潘鉆峰;汪衛(wèi);孟少平;喬治;;混雜聚乙烯醇纖維增強水泥基復合材料力學性能[J];同濟大學學報(自然科學版);2015年01期

2 李俊;孫明清;王應軍;張小玉;劉衡;;SHCC的配制與拉伸性能研究[J];功能材料;2014年21期

3 汪衛(wèi);潘鉆峰;孟少平;喬治;;國產(chǎn)PVA纖維增強水泥基復合材料力學性能研究[J];工業(yè)建筑;2014年S1期

4 李艷;劉澤軍;梁興文;;高性能PVA纖維增強水泥基復合材料單軸受拉特性[J];工程力學;2013年01期

5 李慶華;徐世p，

本文編號：1363063