本文選題：聚乙烯 + 乙烯咔唑　； 參考：《高分子材料科學與工程》2017年05期

【摘要】：為了研究聚乙烯材料的空間電荷特性及力學性能,采用熔融法制備乙烯咔唑(VK)接枝聚乙烯(VK-g-LDPE),并通過電聲脈沖法、差熱掃描量熱法和拉伸試驗對VK-g-LDPE的空間電荷分布、結(jié)晶度和拉伸性能進行了測試。結(jié)果表明,隨著接枝率的增加,對VK-g-LDPE內(nèi)部空間電荷的抑制效果呈現(xiàn)先增強后減弱的趨勢;當接枝率為12.45%時,對VK-gLDPE材料空間電荷的抑制作用最好,試樣的電荷密度最大值僅為0.31 C/m~3,比聚乙烯降低了95.87%;隨著接枝率的增加,VK-g-LDPE的結(jié)晶度呈下降趨勢;隨著接枝率的增加,VK-g-LDPE的拉伸強度呈現(xiàn)先增大后降低的趨勢,且當接枝率為13.02%時達到最大值14.2 N/mm~2;隨著接枝率的增加,VK-g-LDPE的斷裂伸長率和彈性模量呈現(xiàn)下降的趨勢。
[Abstract]:In order to study the space charge characteristics and mechanical properties of polyethylene, vinyl carbazole (VK) grafted polyethylene (VK-g-LDPE) was prepared by melting method. The space charge distribution of VK-g-LDPE was investigated by electroacoustic pulse method, differential scanning calorimetry (DSC) and tensile test. The crystallinity and tensile properties were tested. The results showed that with the increase of grafting rate, the inhibition effect of space charge on VK-g-LDPE showed a tendency of first increasing and then weakening, and when the grafting rate was 12.45%, the inhibitory effect of space charge on VK-gLDPE was the best. The maximum charge density of the sample is only 0.31 C / m ~ (3), which is 95.87% lower than that of polyethylene, and the crystallinity of VK-g-LDPE decreases with the increase of grafting ratio, and the tensile strength of VK-g-LDPE increases first and then decreases with the increase of grafting ratio. When the grafting rate was 13.02, the maximum value was 14.2 N / mmm2, and the elongation at break and elastic modulus of VK-g-LDPE decreased with the increase of grafting rate.
【作者單位】： 哈爾濱理工大學材料科學與工程學院;哈爾濱理工大學工程電介質(zhì)及其應用教育部重點實驗室;
【基金】：哈爾濱理工大學工程電介質(zhì)及其應用教育部重點實驗室開放課題(HUST201401X)
【分類號】：O632.12

【相似文獻】

相關期刊論文 前7條

1 肖祥雄;張興華;;返滴定法測定PP-g-MAH的接枝率[J];化工之友;2007年09期

2 呂恭序;陳文t;李林;;薄膜劑量計聚乙烯-丙烯酸接枝膜的制備及染色[J];北京師范大學學報(自然科學版);1990年01期

3 李艷,褚良銀,朱家驊,夏素蘭,陳文梅,肖新才,曲劍波;溫度感應式開關膜的接枝率對其開關特性的影響[J];化工學報;2004年03期

4 張震亞;張孔祥;岑家聲;劉華平;蔡勇;;在等離子體中纖維素的接枝共聚[J];化學通訊;1986年01期

5 陳榮;譚幗馨;寧成云;尹兆益;張姝江;田冶;關燕霞;;PEGDA/HEMA水凝膠等離子體表面改性的研究[J];離子交換與吸附;2010年02期

6 姚占海,楊慧麗,徐俊;聚丙烯胺肟螯合纖維的輻射合成及對金屬離子的吸附性能[J];輻射研究與輻射工藝學報;1997年03期

7 ;[J];;年期

，

本文編號：1935858