【摘要】：通過熱力學(xué)計算、動力學(xué)試驗以及還原產(chǎn)物微觀形貌掃描電鏡分析,研究Na_2O·Fe_2O_3在Fe_2O_3/MgFe_2O_4-Na_2CO_3-C還原體系中的作用。結(jié)果表明:在該體系中,Na_2CO_3與Fe_2O_3或MgFe_2O_4快速反應(yīng)生成更易被碳還原的Na_2O·Fe_2O_3,從而降低還原反應(yīng)的起始溫度,并加速反應(yīng)的進(jìn)行;Na_2O·Fe_2O_3還能促進(jìn)含鐵礦物碳熱還原過程中鐵晶粒的長大,有利于后續(xù)鐵礦物的磁選分離。
[Abstract]:The role of Na_2O Fe_2O_3 in Fe_2O_3/MgFe_2O_4-Na_2CO_3-C reduction system was studied by thermodynamics calculation, kinetic test and SEM analysis. The results show that in this system, Fe_2O_3 or MgFe_2O_4 can be reacted quickly to produce Na_2O Fe _ 2O _ 3, which is more easily reduced by carbon, thus reducing the initial temperature of the reduction reaction, and accelerating the reaction to accelerate the Na _ 2O Fe_2O_3 can also promote the growth of iron grains in the process of carbothermal reduction of iron bearing minerals. It is advantageous to the separation of iron ore by magnetic separation.
【作者單位】： 中南大學(xué)冶金與環(huán)境學(xué)院;中南大學(xué)難冶有色金屬資源高效利用國家工程實驗室;
【基金】：國家自然科學(xué)基金資助項目(51374239) 中南大學(xué)“創(chuàng)新驅(qū)動計劃”(2015CX001)~~
【分類號】：X756

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 李志生,周敬良;含鐵礦物還原脫砷機(jī)理的探討[J];有色金屬(冶煉部分);1983年06期

，

本文編號：1871333