本文選題：固定化漆酶 + 磁性納米材料��； 參考：《環(huán)境工程》2017年03期

【摘要】：介紹了一種溫和無損固定化漆酶的方法,并研究了其對合成染料的降解行為。首先采用共沉淀法合成乙二胺四乙酸(EDTA)功能化的磁性納米粒子,并以Cu2+為橋基,通過螯合作用將漆酶固載于EDTA功能化的磁性納米粒子表面。通過透射電鏡、紫外-可見光譜儀等對磁性固定化漆酶納米材料進行了表征。固定化漆酶磁性納米材料尺寸在15 nm左右,具有良好的磁響應能力,漆酶固定化率可達223 mg/g;在最佳降解條件下,其對孔雀石綠和堿性品紅均表現(xiàn)出良好的降解能力;同時固定化漆酶具有較高的穩(wěn)定性和重復使用性,便于回收利用。
[Abstract]:A mild and nondestructive immobilization method of laccase was introduced, and the degradation behavior of synthetic dyes was studied.Firstly, the ethylenediamine tetraacetic acid (EDTA) functionalized magnetic nanoparticles were synthesized by co-precipitation method, and the laccase was immobilized on the surface of EDTA functionalized magnetic nanoparticles by chelating with Cu2 as the bridge.Magnetic immobilized laccase nanomaterials were characterized by transmission electron microscopy (TEM) and UV-vis spectrometer.The size of immobilized laccase magnetic nanomaterials is about 15 nm and has good magnetic response. The immobilization rate of laccase can reach 223 mg / g. Under the optimum degradation conditions, the immobilized laccase shows good degradation ability to both malachite green and alkaline fuchsin.At the same time, the immobilized laccase has high stability and reusability, which is easy to recycle.
【作者單位】： 新疆產(chǎn)品質量監(jiān)督檢驗研究院;新疆恒正司法鑒定中心;
【基金】：國家自然科學基金項目(21177013)
【分類號】：X703;TB383.1

【相似文獻】

相關期刊論文 前10條

1 江強;周細應;;磁性納米材料的制備及其在軍事上的應用[J];材料科學與工程學報;2012年03期

2 劉苗;杜卓;李攻科;;磁性納米材料在樣品前處理中的應用進展[J];分析科學學報;2012年03期

3 ;書刊征訂[J];分析化學;2013年07期

4 ;生物醫(yī)用磁性納米材料與器件[J];生物技術通訊;2013年06期

5 陳功;殷s，

本文編號：1758804