本文選題：二鉬酸銨 + 溶解度　； 參考：《西安科技大學學報》2017年03期

【摘要】：采用靜態(tài)平衡法測定了pH值在8.5~9.0之間的二鉬酸銨-氨-水三元體系固液相平衡及介穩(wěn)區(qū),分別用Apelblat簡化方程和λh方程對相平衡數(shù)據(jù)進行關(guān)聯(lián),結(jié)果表明,2種模型關(guān)聯(lián)標準方差分別為1.626%和1.661%。同時,采用濁度法測定了二鉬酸銨的結(jié)晶介穩(wěn)區(qū)數(shù)據(jù),考察了降溫速率對介穩(wěn)區(qū)的影響,推導出二鉬酸銨在氨水體系中的結(jié)晶成核級數(shù)。
[Abstract]:The solid-liquid equilibrium and metastable regions of ammonium dimolybdate ammonia-water ternary system with pH between 8.5 and 9.0 were determined by static equilibrium method. The phase equilibrium data were correlated by Apelblat simplified equation and 位 h equation, respectively. The results showed that the correlation standard variance of the two models was 1.626% and 1.661respectively. At the same time, the data of crystal metastable zone of ammonium dimolybdate were determined by turbidimetric method. The effect of cooling rate on the metastable zone was investigated. The nucleation order of ammonium dimolybdate in ammonia water system was deduced.
【作者單位】： 天津科技大學化工與材料學院;金堆城鉬業(yè)股份有限技術(shù)中心;金堆城鉬業(yè)股份有限公司化學分公司;
【分類號】：TQ113.79

【相似文獻】

相關(guān)期刊論文 前10條

1 緒小鵬;優(yōu)質(zhì)鉬酸銨是鉬條生產(chǎn)的質(zhì)量保證[J];中國鉬業(yè);1997年Z1期

2 荊春生;我國鉬酸銨生產(chǎn)現(xiàn)狀綜述[J];中國鉬業(yè);2000年06期

3 樊建軍,荊春生;高鉀鉬酸銨制備新工藝研究[J];應(yīng)用化工;2004年01期

4 張文鉦;鉬酸銨研發(fā)進展[J];中國鉬業(yè);2005年02期

5 陳懷杰;王繼民;林恬盛;李杏英;;用粗鉬酸制備鉬酸銨工藝的研究[J];材料研究與應(yīng)用;2007年03期

6 曹璇;張寶;;七鉬酸銨的制備及進展[J];銅業(yè)工程;2008年04期

7 李輝;唐麗霞;;鉬酸銨生產(chǎn)工藝與技術(shù)進展狀況分析[J];中國鉬業(yè);2009年06期

8 周新文;王磊;唐麗霞;;離子交換法除雜制備鉬酸銨[J];中國鉬業(yè);2011年03期

9 張亨;;鉬酸銨的生產(chǎn)研究綜述[J];杭州化工;2012年02期

10 李來平;劉燕;王國棟;張文鉦;;鉬酸銨生產(chǎn)技術(shù)發(fā)展現(xiàn)狀[J];無機鹽工業(yè);2012年08期

相關(guān)碩士學位論文 前2條

1 郭彥輝;二鉬酸銨結(jié)晶過程控制及形成單晶的工藝條件研究[D];河南科技大學;2012年

2 韓凌;pH調(diào)節(jié)法去除鉬酸銨中微量鎢的研究[D];東北大學;2009年

，

本文編號：1829153