【摘要】：采用疲勞試驗、透射電鏡、掃描電鏡及X射線衍射儀等方法研究了2124-T851鋁合金厚板不同參數(shù)孔擠壓強化后疲勞壽命與顯微組織的變化。結(jié)果表明:孔擠壓強化后試樣的疲勞壽命先隨擠壓量的增大而升高,隨后又迅速降低,擠壓量為0.4 mm時疲勞壽命達到峰值,較未強化增加12.66倍;組織觀察結(jié)果表明孔擠壓強化后,在孔壁強化層內(nèi)形成了位錯胞狀結(jié)構(gòu)和殘余壓應(yīng)力,并且隨擠壓量增大先迅速增加然后趨于平緩,強化層的形成可以有效延緩疲勞裂紋的擴展速率;同時,適當(dāng)?shù)目讛D壓強化可改善表面粗糙度,降低裂紋萌生幾率,從而提高材料的疲勞壽命。
[Abstract]:The changes of fatigue life and microstructure of 2124-T851 aluminum alloy thick plate were studied by means of fatigue test, transmission electron microscopy, scanning electron microscope and X-ray diffractometer. The results show that the fatigue life of the specimens increases with the increase of extrusion volume, and then decreases rapidly. The fatigue life reaches the peak value when the extrusion amount is 0.4 mm, which is 12.66 times higher than that of the unstrengthened samples. The results of microstructure observation show that the dislocation cellular structure and residual compressive stress are formed in the strengthened layer of hole wall after extrusion strengthening, and then increase rapidly with the increase of extrusion volume and then tend to smooth. The formation of strengthened layer can effectively delay the growth rate of fatigue crack. At the same time, proper hole extrusion strengthening can improve the surface roughness, reduce the crack initiation probability, and thus improve the fatigue life of the material.
【作者單位】： 北京航空材料研究院;
【分類號】：V261;V252.2

【相似文獻】

相關(guān)期刊論文 前10條

1 曾春華;鄧蓉英;杜金聲;伍義生;;變幅載荷下疲勞壽命的估算與影響因素[J];航空學(xué)報;1979年03期

2 曾春華;;在復(fù)雜載荷歷史下缺口元件疲勞壽命的預(yù)計[J];機械強度;1981年01期

3 邵亞生,楊慶雄;釘載孔擠壓強化元件疲勞壽命研究[J];航空學(xué)報;1990年12期

4 董聰,楊慶雄;結(jié)構(gòu)系統(tǒng)疲勞壽命可靠性分析理論與算法[J];航空學(xué)報;1993年05期

5 劉東星;陶華;劉早立;劉風(fēng)雷;;干涉量對復(fù)合材料層合板疲勞壽命的影響[J];航空制造技術(shù);2011年08期

6 劉兵吉;渦輪葉片疲勞壽命公式及可靠性預(yù)測方法[J];推進技術(shù);1989年05期

7 劉萍,張開達;干涉對復(fù)合材料疊層板螺栓連接疲勞強度的影響[J];航空學(xué)報;1991年12期

8 余春華;尹曉春;瞿元;沈培良;董雪花;;飛機普通框疲勞壽命的三維有限元分析[J];航空維修與工程;2006年03期

9 賀小帆;劉文s，

本文編號：2467731