本文選題：AS滲透養(yǎng)護(hù)劑 + 預(yù)防性養(yǎng)護(hù)��； 參考：《長沙理工大學(xué)》2015年碩士論文

【摘要】：CO-MA-SEAL?Asphalt Seal(以下簡稱AS)滲透養(yǎng)護(hù)劑是一種富含納米顆粒的特殊活性化學(xué)反應(yīng)成分的滲透性水性產(chǎn)品。AS滲透養(yǎng)護(hù)劑因其優(yōu)良的滲透流動性、分散性、抗剝落和抗磨耗等性能在國外得到廣泛關(guān)注和應(yīng)用,而國內(nèi)對其的認(rèn)識才剛剛起步。為此,本文依托湖南省臨長高速公路路面中修工程試驗(yàn)段,對AS滲透養(yǎng)護(hù)劑在瀝青路面預(yù)養(yǎng)護(hù)工程中的應(yīng)用技術(shù)開展研究。(1)根據(jù)修復(fù)機(jī)理研究表明,AS滲透養(yǎng)護(hù)劑在防治水損害、提高高溫穩(wěn)定性及修復(fù)微小裂縫方面有著特殊優(yōu)勢。AS滲透養(yǎng)護(hù)劑的性能檢驗(yàn)表明,其符合界面滲透型防水涂料技術(shù)性能的評定標(biāo)準(zhǔn)。(2)通過原材料物理力學(xué)性能檢驗(yàn)表明,SBS改性瀝青和各檔集料的物理力學(xué)性能均能滿足設(shè)計要求。同時,采用馬歇爾設(shè)計法,確定了SBS改性AC-13C瀝青混合料的設(shè)計配合比。對AS滲透養(yǎng)護(hù)劑涂刷前后的混合料進(jìn)行了路用性能對比試驗(yàn),結(jié)果表明,涂刷AS滲透養(yǎng)護(hù)劑后,混合料抗磨耗能力及抗?jié)B性能得到顯著改善,抗滑性能受到一定影響,而對材料的高溫穩(wěn)定性、低溫抗裂性及水穩(wěn)定性等的改善效果并不顯著。(3)根據(jù)依托工程現(xiàn)場實(shí)際施工情況,提出了AS滲透養(yǎng)護(hù)劑的施工工序、工藝及注意事項,通過試驗(yàn)段現(xiàn)場檢驗(yàn),對實(shí)體工程中AS滲透養(yǎng)護(hù)劑涂刷前后的使用性能進(jìn)行了對比分析,進(jìn)一步確定了其應(yīng)用效果,并對AS滲透養(yǎng)護(hù)劑作為新舊瀝青層促粘劑和路面離析修補(bǔ)劑的施工方法進(jìn)行了補(bǔ)充介紹。(4)通過噴灑AS滲透養(yǎng)護(hù)劑和常用的預(yù)防性養(yǎng)護(hù)措施的經(jīng)濟(jì)比較分析,可知AS滲透養(yǎng)護(hù)劑材料具有顯著經(jīng)濟(jì)效益,施工工藝簡單,產(chǎn)品安全環(huán)保無污染,對交通影響小,是一種優(yōu)質(zhì)的瀝青路面預(yù)養(yǎng)護(hù)材料,具有廣泛的應(yīng)用前景。綜上所述,使用AS滲透養(yǎng)護(hù)劑對瀝青路面進(jìn)行預(yù)防性養(yǎng)護(hù)能有效延長路用壽命,且經(jīng)濟(jì)合理,因此本文的研究結(jié)果可為AS滲透養(yǎng)護(hù)劑的進(jìn)一步推廣應(yīng)用提供參考。
[Abstract]:The osmotic curing agent of CO-MA-SEAL?Asphalt is a kind of permeable water-based product rich in special active chemical reaction composition of nanoparticles. The permeability curing agent of as has excellent permeation fluidity and dispersity. The properties of anti-peeling and anti-wear have been widely paid attention to and applied abroad, but the understanding of them in China is just beginning. In this paper, based on the experimental section of Hunan Linchang Expressway pavement repair Project, the application technology of as osmotic curing agent in asphalt pavement pre-maintenance engineering is studied. 1) according to the research of repairing mechanism, it is shown that as permeable curing agent is preventing water damage. There are special advantages in improving high temperature stability and repairing micro cracks. The performance test of as osmotic curing agent shows that, It accords with the technical performance evaluation standard of interfacial permeable waterproof coating. The physical and mechanical properties of SBS modified asphalt and aggregate can meet the design requirements through the physical and mechanical properties test of raw materials. At the same time, Marshall design method is used to determine the design mix ratio of SBS modified AC-13C asphalt mixture. The contrasting tests on the pavement performance of the mixture before and after as permeation curing agent are carried out. The results show that the wear resistance and impermeability of the mixture are obviously improved and the skid resistance is affected to some extent after the as permeable curing agent is brushed. However, the improvement of material stability at high temperature, crack resistance at low temperature and water stability is not significant. According to the actual construction situation of supporting project, the construction procedure, process and attention of as permeable curing agent are put forward. Through the field inspection of the test section, the performance of as penetration curing agent before and after brushing in solid engineering is compared and analyzed, and the application effect is further determined. The construction method of as permeable curing agent as new and old asphalt layer adhesive and pavement segregation mending agent is introduced in this paper. The economic comparison and analysis of spraying as permeation curing agent and common preventive maintenance measures are carried out. It can be seen that as permeable curing agent material has remarkable economic benefit, simple construction technology, safe, environmental protection and no pollution, and has little influence on traffic. It is a kind of high quality asphalt pavement pre-maintenance material and has a wide application prospect. To sum up, preventive maintenance of asphalt pavement with as osmotic curing agent can effectively prolong the service life of asphalt pavement and is economical and reasonable. Therefore, the research results of this paper can provide a reference for the further popularization and application of as osmotic curing agent.
【學(xué)位授予單位】：長沙理工大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2015
【分類號】：U418.6;U416.217

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 覃立香,楊德坡;混凝土養(yǎng)護(hù)劑的發(fā)展及應(yīng)用[J];國外建材科技;1999年04期

2 屈志中;混凝土養(yǎng)護(hù)劑研究和應(yīng)用的若干問題[J];建筑技術(shù);2001年01期

3 傅智,劉云,夏玲玲,牛開民;《水泥混凝土養(yǎng)護(hù)劑》標(biāo)準(zhǔn)的編制介紹[J];施工技術(shù);2003年02期

4 ;混凝土養(yǎng)護(hù)劑[J];建材工業(yè)信息;2003年11期

5 朱志遠(yuǎn);《水泥混凝土養(yǎng)護(hù)劑》等行業(yè)標(biāo)準(zhǔn)已批準(zhǔn)實(shí)施[J];中國建筑防水;2003年07期

6 嚴(yán)忠;王亮;;新型養(yǎng)護(hù)劑的研究及推廣[J];新疆石油科技;2003年01期

7 于素健;盧丹;李保華;遲培云;;高性能養(yǎng)護(hù)劑的自養(yǎng)原理及其技術(shù)經(jīng)濟(jì)性探討[J];混凝土;2007年09期

8 汪志芳;;淺談混凝土養(yǎng)護(hù)劑在公路建設(shè)及民用建筑中的應(yīng)用[J];北方交通;2009年06期

9 亓良樹;;高效多功能養(yǎng)護(hù)劑的研究與應(yīng)用[J];混凝土世界;2009年10期

10 張振雷;金恒剛;石中濤;張大利;;混凝土養(yǎng)護(hù)劑應(yīng)用技術(shù)研究[J];遼寧建材;2011年03期

相關(guān)會議論文 前1條

1 周子昌;劉衛(wèi)東;謝文杰;;混凝土養(yǎng)護(hù)劑的研究[A];第五屆全國混凝土耐久性學(xué)術(shù)交流會論文集[C];2000年

相關(guān)重要報紙文章 前5條

1 記者 盧育輝 通訊員唐明勇 蘇卓;植物多功能養(yǎng)護(hù)劑受青睞[N];廣東科技報;2008年

2 趙引德 蔡磊;新型植物養(yǎng)護(hù)劑及技術(shù)研制成功[N];農(nóng)資導(dǎo)報;2007年

3 建材;新型砼養(yǎng)護(hù)劑在桂林研制成功[N];中華建筑報;2001年

4 駐廣西記者 劉保和;傳統(tǒng)砼養(yǎng)護(hù)方式將被淘汰[N];中國建材報;2001年

5 水建;混凝土有了“保濕霜”[N];中國冶金報;2004年

相關(guān)碩士學(xué)位論文 前4條

1 黃楊英子;AS滲透養(yǎng)護(hù)劑在瀝青路面預(yù)養(yǎng)護(hù)中的應(yīng)用研究[D];長沙理工大學(xué);2015年

2 薛斌;復(fù)合型混凝土養(yǎng)護(hù)劑的制備及性能研究[D];長安大學(xué);2014年

3 田珂;瀝青路面光屏蔽預(yù)養(yǎng)護(hù)劑組分優(yōu)化與路用性能研究[D];長安大學(xué);2014年

4 韓聰聰;施工階段水泥混凝土路面噴灑養(yǎng)護(hù)技術(shù)研究[D];河北工業(yè)大學(xué);2014年

，

本文編號：1782655