本文選題：Cr-Al納米棒 + 微波合成技術(shù)��； 參考：《中國陶瓷》2017年03期

【摘要】：采用微波熱處理技術(shù)得到了Cr-Al納米棒。采用XRD、掃描電鏡與能譜儀研究產(chǎn)物的物相組成與顯微形貌。研究結(jié)果表明,通過微波合成技術(shù),采用2Cr/Al/石墨扮體原料反應(yīng)后的產(chǎn)物的主相為Cr_2Al、Cr_7C_3和Cr_2AlC。產(chǎn)物中存在許多20~30μm長的毛茸茸狀組織,該組織中是由大量CrAl納米棒構(gòu)成的。Cr-Al納米棒的長度約200~500 nm,寬度約100nm。當(dāng)用碳纖維取代石墨扮體時,除了產(chǎn)生大量的Cr-Al納米棒,還會產(chǎn)生大量的Al_2O_3晶須。原料中的石墨或碳纖維起到了誘發(fā)電弧放電的作用,從而促進(jìn)CrAl納米棒的形成。
[Abstract]:Cr-Al nanorods were obtained by microwave heat treatment. The phase composition and morphology of the products were studied by XRD, SEM and EDS. The results show that by microwave synthesis, the main phases of the products after the reaction of 2Cr / Al / graphite as raw materials are Cr2AlSZ / Cr7Cs3 and Cr2AlC3. The results show that the main phases of the products are Cr2AlS-1, Cr2AlC3 and Cr2AlC. There are a lot of furry tissues of 20 ~ 30 渭 m long in the product. The length and width of .Cr-Al nanorods are about 200 ~ 500 nm and 100 nm respectively, which are made up of a large number of Cr-Al nanorods. When carbon fiber is used to replace graphite, a large number of Al _ 2O _ 3 whiskers will be produced in addition to a large number of Cr-Al nanorods. Graphite or carbon fiber in the raw material can induce arc discharge and promote the formation of CrAl nanorods.
【作者單位】： 中原工學(xué)院材料與化工學(xué)院;金剛石技術(shù)國家地方聯(lián)合工程實驗室;
【基金】：鄭州市國際科技合作與交流項目(153PGJHZ209) 河南省高等學(xué)校重點科研項目(17A430034) 河南省高校創(chuàng)新團(tuán)隊項目(15IRTSTHN004) 河南省省院科技合作項目(142106000193) 河南省教育廳自然科學(xué)研究計劃項目資助(14A430007) 河南省科技開放合作項目(142106000051) 鄭州市人才引育項目(141PRCYY514)
【分類號】：TB383.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前5條

1 潘冶,張傳,張衍誠,孫國雄;Cr-Al(Cr)_2O_3金屬陶瓷的燃燒合成與致密化[J];金屬學(xué)報;2005年07期

2 ;Cr-Al系海洋結(jié)構(gòu)鋼及其耐蝕性探討[J];上海鋼研;1976年02期

3 尹士科,張忠文,王先禮;Cr-Al鋼焊接熱影響區(qū)沖擊韌性研究[J];鋼鐵研究學(xué)報;1991年03期

4 林煒,穆暢道,張銘讓;溶液中Cr-Al異金屬配合物的形成及穩(wěn)定性研究[J];中國皮革;2003年03期

5 ;[J];;年期

，

本文編號：2082566