【摘要】：普通砂漿在施工的時(shí)候,等砂漿拌制好以后,按照施工方法,通常要經(jīng)過人工攤鋪、刮平、抹面,在砂漿終凝以前還要做三遍壓光等工序,這種分層施工的方法有很多弊端,自流平砂漿可以很好的解決這些問題。水泥基自流平砂漿施工時(shí),只需稍加鋪攤就可以自動(dòng)流平,自流平砂漿具有耐磨性,既可作為基層也可以作為面層,抗?jié)B性能可以有效的防止?jié)B漏,由于是單層施工,避免了開裂、凹凸不平、破損等缺陷,是未來(lái)地面找平材料發(fā)展的方向。摻入粉煤灰和礦渣粉既可以降低生產(chǎn)成本,又可以提高砂漿的后期強(qiáng)度,脫硫石膏參與水化形成鈣礬石,減小了砂漿的收縮,使砂漿的收縮率維持在國(guó)標(biāo)要求的0.15%以內(nèi),實(shí)驗(yàn)在保證抗壓抗折強(qiáng)度的基礎(chǔ)上,利用正交表分析了流動(dòng)度較好的礦物摻合料摻量,加入硫鋁酸鹽水泥和早強(qiáng)劑提高砂漿的一天強(qiáng)度,聚羧酸減水劑取代萘系減水劑進(jìn)一步提高砂漿的流動(dòng)度,摻入消泡劑降低孔隙率,使砂漿更加密實(shí),防水效果更好。結(jié)果表明：①粉煤灰和石膏摻入后砂漿強(qiáng)度降低,石膏可減小砂漿收縮,礦渣粉活性較高,10wt%摻量時(shí)的強(qiáng)度比5wt%和7.5wt%要好,摻合料的合理搭配可有效提高砂漿的流動(dòng)度。②硫鋁酸鹽水泥摻量增加,砂漿1d強(qiáng)度增大,摻量超過11wt%時(shí),砂漿水化加快,離析狀況和表面起皮、泛堿現(xiàn)象消失,流動(dòng)度降低到130mm以下。③聚羧酸減水劑分散作用強(qiáng),可將砂漿流動(dòng)度提高到140mm以上,但會(huì)引發(fā)離析,纖維素醚具有保水、增稠作用,但會(huì)延緩水泥的水化,隨乳膠粉摻量增加,砂漿強(qiáng)度下降。④NC強(qiáng)劑可將砂漿1d抗折和抗壓強(qiáng)度提高到2MPa和6MPa以上,但對(duì)1d強(qiáng)度的增加有限,隨著摻量的增加,漿體凝結(jié)速度加快,稠度增加,流動(dòng)度下降,離析現(xiàn)象消失。⑤消泡劑摻入后,砂漿孔隙率降低,流動(dòng)度增大,砂漿更加密實(shí),抗壓抗折強(qiáng)度增大,抗?jié)B壓強(qiáng)增大。依據(jù)《JCT985-2005地面用水泥基自流平砂漿》和《JCT2090-2011聚合物防水漿料》可知,通過正交實(shí)驗(yàn)分析和單因素實(shí)驗(yàn)分析,最后得出的最優(yōu)配比的抗折抗壓強(qiáng)度,流動(dòng)度,尺寸變化率和砂漿試件抗?jié)B性能均能達(dá)到要求。
[Abstract]:When the ordinary mortar is in construction, and after the mortar has been mixed well, according to the construction method, it usually has to go through manual spreading, scraping, polishing, and three times pressing before the mortar is finally solidified. This method of layered construction has many disadvantages. Self-leveling mortar can solve these problems well. In the construction of cement base self-leveling mortar, it can be flattened automatically with a little spreading stand. The self-leveling mortar has wearability, which can be used either as the base or as the surface layer. The impermeability can effectively prevent leakage, because it is a single-layer construction. Avoid cracking, uneven, damaged and other defects, is the future development direction of leveling materials. The addition of fly ash and slag powder can not only reduce the production cost, but also improve the later strength of mortar. Desulphurization gypsum takes part in hydration to form ettringite, which reduces the shrinkage of mortar and keeps the shrinkage of mortar within 0.15% of the national standard. On the basis of guaranteeing compressive and flexural strength, the authors analyzed the content of mineral admixture with good fluidity by orthogonal table, and added sulphoaluminate cement and early strength agent to improve the daily strength of mortar. The polycarboxylic acid superplasticizer replaces the naphthalene series water reducing agent to further improve the flowing degree of mortar, add defoamer to reduce porosity, make mortar more dense and waterproof effect better. The results show that: (1) the strength of mortar decreases after the addition of fly ash and gypsum, the shrinkage of mortar is reduced by gypsum, the activity of slag powder is higher, and the strength of 10 wt% is better than that of 5wt% and 7.5wt%. The reasonable mix of admixtures can effectively improve the fluidity of mortar. 2 when the content of sulphoaluminate cement is increased and the strength of mortar increases in one day, the hydration of mortar is accelerated, the segregation condition and surface exfoliation are increased, and the pan-alkali phenomenon disappears when the admixture is more than 11wt%. When the fluidity decreases below 130mm, the dispersion of polycarboxylic acid water reducer is strong, which can increase the flowing degree of mortar to above 140mm, but it will cause segregation. Cellulose ether has the function of keeping water and thickening, but it will delay the hydration of cement, and with the increase of the amount of latex powder, The strength of mortar decreases. 4NC can increase the flexural strength and compressive strength of mortar to more than 2MPa and 6MPa, but the increase of 1d strength is limited. With the increase of content, the setting speed of mortar increases, the consistency increases and the mobility decreases. After the addition of defoamer, the porosity of mortar decreases, the fluidity increases, the mortar becomes more dense, the compressive strength increases and the impermeability pressure increases. According to < JCT985-2005 cement based self-leveling mortar > and < JCT2090-2011 polymer waterproof slurry >, through orthogonal experimental analysis and single factor experimental analysis, the best ratio of flexural compressive strength and fluidity is obtained. The size change rate and impermeability of mortar can meet the requirements.
【學(xué)位授予單位】：濟(jì)南大學(xué)
【學(xué)位級(jí)別】：碩士
【學(xué)位授予年份】：2015
【分類號(hào)】：TU578.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 楊崇豪;顏承越;郭險(xiǎn)峰;;高摻量原狀粉煤灰砂漿的性能研究及應(yīng)用[J];華北水利水電學(xué)院學(xué)報(bào);1988年02期

2 顏承越;;砂漿強(qiáng)度為什么高低不穩(wěn)定[J];建筑工人;1989年08期

3 顏承越;高摻量原狀粉煤灰砂漿的試驗(yàn)研究[J];施工技術(shù);1989年05期

4 尹志府;山砂砂漿摻Ⅲ級(jí)粉煤灰后的強(qiáng)度效應(yīng)[J];四川建筑科學(xué)研究;1991年03期

5 王品倫;建筑干砂漿的研制[J];新型建筑材料;2001年11期

6 張斌,張明;粉煤灰在砂漿中的應(yīng)用[J];山西建筑;2001年06期

7 孫玉健,張照武,王朝釩;“新型砂漿”的試驗(yàn)研究與應(yīng)用[J];山東電力高等�？茖W(xué)校學(xué)報(bào);2001年01期

8 張彩霞,馮學(xué)亮,羅梅,楚葳蕤,張軍;摻微沫劑砂漿的配合比設(shè)計(jì)[J];河南建材;2001年03期

9 張林;高強(qiáng)大稠度砂漿的試驗(yàn)和應(yīng)用[J];廣西城鎮(zhèn)建設(shè);2003年09期

10 陳萌,王仁義,彭少民;點(diǎn)荷法砂漿強(qiáng)度的簡(jiǎn)化換算公式[J];武漢理工大學(xué)學(xué)報(bào);2004年02期

相關(guān)會(huì)議論文 前10條

1 高文武;高秀峰;;一種兼具有防氡功能的節(jié)能型室內(nèi)用砂漿的研[A];07’中國(guó)西安能源動(dòng)力科技創(chuàng)新研討會(huì)及展示會(huì)論文集[C];2007年

2 梁建國(guó);龍小清;程少輝;;不同底模砂漿強(qiáng)度試驗(yàn)研究[A];砌體結(jié)構(gòu)理論與新型墻材應(yīng)用[C];2007年

3 楊春俠;楊偉軍;施楚賢;;高強(qiáng)高性能砂漿的研究[A];第十一屆全國(guó)結(jié)構(gòu)工程學(xué)術(shù)會(huì)議論文集第Ⅰ卷[C];2002年

4 李娟;賈智勛;;盲目使用“砂漿王”的危害及預(yù)防[A];土木建筑學(xué)術(shù)文庫(kù)（第16卷）[C];2012年

5 楊建江;楊琳;;回彈法、剪切法測(cè)砂漿強(qiáng)度的試驗(yàn)研究及測(cè)強(qiáng)曲線繪制[A];第二屆全國(guó)工程結(jié)構(gòu)抗震加固改造技術(shù)交流會(huì)論文集[C];2010年

6 汪峻峰;;一種高性能砂漿/混凝土的應(yīng)用研究[A];高強(qiáng)與高性能混凝土及其應(yīng)用——第七屆全國(guó)高強(qiáng)與高性能混凝土學(xué)術(shù)交流會(huì)論文集[C];2010年

7 王維;王曉丹;袁濤;甘萬(wàn)貴;唐嵐;;鋼渣砂干混地坪砂漿的制備及性能研究[A];商品砂漿的科學(xué)與技術(shù)[C];2011年

8 孫杰;王培銘;劉賢萍;龐敏;;粉煤灰、礦渣的化學(xué)組分對(duì)水泥砂漿強(qiáng)度的影響[A];房建材料與綠色建筑[C];2009年

9 彭方靈;劉興華;;高性能修補(bǔ)砂漿研制開發(fā)[A];第三屆全國(guó)建筑結(jié)構(gòu)技術(shù)交流會(huì)論文集[C];2011年

10 李赫;;水泥雙灰粉砂漿試驗(yàn)研究[A];高性能混凝土的研究與應(yīng)用——第五屆全國(guó)高性能混凝土學(xué)術(shù)交流會(huì)論文[C];2004年

相關(guān)重要報(bào)紙文章 前4條

1 邵鋒燕;離析是怎樣產(chǎn)生的[N];中華建筑報(bào);2011年

2 王祥;南京亞宙公司 研制出新一代砂漿保水增塑劑[N];中華建筑報(bào);2010年

3 駐遼寧記者 李一;新型建材重“綠色”[N];中國(guó)建材報(bào);2006年

4 王建龍 楊建榮;磚石砌體質(zhì)量通病的防治[N];建筑時(shí)報(bào);2006年

相關(guān)博士學(xué)位論文 前4條

1 于本田;基于緩凝砂漿包裹的緩粘結(jié)預(yù)應(yīng)力筋粘結(jié)性能試驗(yàn)研究[D];蘭州交通大學(xué);2014年

2 楊鉆;高強(qiáng)微生物砂漿機(jī)理與工作性能研究[D];清華大學(xué);2013年

3 賈興文;含F(xiàn)e_（1-δ）O廢渣砂漿的導(dǎo)電性和機(jī)敏性研究[D];重慶大學(xué);2009年

4 徐洪;砂漿錨桿錨固體耐久性基礎(chǔ)研究[D];重慶大學(xué);2009年

相關(guān)碩士學(xué)位論文 前10條

1 林含;高鐵盆式橡膠支座用砂漿的性能研究[D];北京建筑大學(xué);2015年

2 王耀增;高性能水泥基快速修補(bǔ)料的性能研究[D];哈爾濱工業(yè)大學(xué);2015年

3 高峰;基于修補(bǔ)加固的聚合物纖維砂漿研究[D];南昌大學(xué);2015年

4 王濤;基于吸水特性的磚砌體現(xiàn)場(chǎng)砂漿強(qiáng)度及其檢測(cè)方法研究[D];長(zhǎng)沙理工大學(xué);2014年

5 馬大勇;水泥砂漿的幾個(gè)關(guān)鍵性能研究[D];清華大學(xué);2014年

6 王曉瑩;早齡期高性能約束砂漿環(huán)開裂機(jī)制數(shù)值模擬[D];重慶大學(xué);2015年

7 華騰飛;組成材料及工藝條件對(duì)混凝土結(jié)構(gòu)修補(bǔ)砂漿性能的影響研究[D];重慶大學(xué);2015年

8 劉輝;砌體砂漿強(qiáng)度檢測(cè)的原位拔出法研究[D];中國(guó)海洋大學(xué);2015年

9 肖建強(qiáng);水硬性石灰的設(shè)計(jì)制備與性能研究[D];東南大學(xué);2015年

10 劉闖;水泥基自流平防水抗?jié)B砂漿的制備與性能研究[D];濟(jì)南大學(xué);2015年

，

本文編號(hào)：2337645