本文關(guān)鍵詞：工程纖維增強(qiáng)水泥基復(fù)合材料PVA-ECC力學(xué)性能研究　出處：《河南理工大學(xué)》2015年碩士論文　論文類型：學(xué)位論文

  更多相關(guān)文章： 工程纖維增強(qiáng)水泥基復(fù)合材料 PVA纖維 力學(xué)性能 強(qiáng)度 變形 本構(gòu)方程

【摘要】：工程纖維增強(qiáng)水泥基復(fù)合材料(Engineered Fiber Reinforced Cementitious Composites)PVA-ECC,是一種高性能纖維增強(qiáng)水泥基復(fù)合材料,在拉伸荷載作用下具有應(yīng)變-硬化和多微縫開裂特性,克服了現(xiàn)有混凝土材料的抗拉、抗剪強(qiáng)度低,抗震性能較差的缺點(diǎn),是一種環(huán)保生態(tài)型建筑材料。該材料有望解決混凝土所面臨的安全性、耐久性問題,本文通過(guò)試驗(yàn)對(duì)PVA-ECC的力學(xué)性能進(jìn)行了一系列的研究,主要研究?jī)?nèi)容如下:(1)通過(guò)單軸抗拉性能試驗(yàn),研究了PVA纖維體積率、水膠比、砂膠比等對(duì)PVA-ECC單軸受拉強(qiáng)度和變形的影響,合理描述了PVA-ECC受拉應(yīng)變硬化過(guò)程。根據(jù)實(shí)測(cè)單軸受拉應(yīng)力-應(yīng)變曲線的特點(diǎn),對(duì)PVA-ECC應(yīng)變軟化前的應(yīng)力-應(yīng)變關(guān)系進(jìn)行了合理地簡(jiǎn)化,并提出了相應(yīng)單軸受拉本構(gòu)方程。(2)通過(guò)劈裂抗拉性能試驗(yàn),研究了PVA纖維體積率、水膠比等對(duì)PVA-ECC劈裂抗拉強(qiáng)度和變形的影響,根據(jù)所測(cè)得的試驗(yàn)結(jié)果,建立了劈裂受拉強(qiáng)度與單軸受拉強(qiáng)度之間的關(guān)系。(3)通過(guò)單軸受壓性能試驗(yàn),研究了PVA纖維體積率、水膠比、砂膠比、加載速率、尺寸效應(yīng)等對(duì)PVA-ECC單軸受壓強(qiáng)度和變形的影響;根據(jù)所測(cè)得的試驗(yàn)結(jié)果,建立了軸心抗壓強(qiáng)度與立方體抗壓強(qiáng)度的關(guān)系;并根據(jù)實(shí)測(cè)軸心受壓應(yīng)力-應(yīng)變曲線的特點(diǎn),提出了PVA-ECC單軸受壓本構(gòu)方程。(4)通過(guò)常規(guī)三軸受壓性能試驗(yàn),研究了不同水膠比下的圓柱體試件在0~25MPa不同圍壓下的常規(guī)三軸受壓性能,根據(jù)所測(cè)得的試驗(yàn)結(jié)果,建立了PVA-ECC極限抗壓強(qiáng)度、峰值應(yīng)變、以及極限應(yīng)變與側(cè)向圍壓之間的關(guān)系,并根據(jù)實(shí)測(cè)應(yīng)力-應(yīng)變曲線,提出了PVA-ECC常規(guī)三軸受壓本構(gòu)方程。
[Abstract]:Engineering fiber reinforced cement composite (Engineered Fiber Reinforced Cementitious Composites PVA-ECC), is a kind of high performance fiber reinforced cement composites under tensile load with strain hardening and multiple cracking characteristics, overcomes the defects of the existing concrete tensile strength, low shear strength, seismic performance is poor, is a kind of environmental ecological building materials. The material is expected to solve the safety of concrete facing, the durability problem, this paper through a series of mechanical performance test of PVA-ECC, the main research contents are as follows: (1) the performance of uniaxial tensile test of PVA fiber volume ratio, water binder ratio, ratio on the PVA-ECC of uniaxial tensile strength and deformation affected by sand adhesive, reasonable description of the tensile strain hardening process by PVA-ECC. According to the measured uniaxial tensile stress strain curve, the PVA-ECC should be The strain softening stress-strain relations are reasonably simplified, and put forward the corresponding uniaxial tension constitutive equation. (2) by splitting tensile performance test of PVA fiber volume ratio, water cement ratio on the PVA-ECC splitting effect and deformation of the tensile strength, according to the test results measured the established relationship between splitting tensile strength and uniaxial tensile strength. (3) the performance of uniaxial compression test of PVA fiber volume ratio, water cement ratio, sand cement ratio, loading rate, size effect and deformation effect on uniaxial compressive strength test according to PVA-ECC; the measured results, to establish the relationship between the compressive strength and compressive strength; and the characteristics of stress-strain curve according to measured axial compression, the constitutive equation of PVA-ECC under uniaxial compression. (4) by conventional three axis compression performance test of different water binder ratio of cylinder specimen In the 0~25MPa under different confining pressure of the conventional three axis compression performance, according to the test results measured, established the compressive strength, peak strain and PVA-ECC limit, limit strain and confining pressure relationship between, and according to the measured stress-strain curves, the constitutive equation of PVA-ECC conventional three axis compression.

【學(xué)位授予單位】：河南理工大學(xué)
【學(xué)位級(jí)別】：碩士
【學(xué)位授予年份】：2015
【分類號(hào)】：TU528

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 徐亦冬;何山青;;流變學(xué)在水泥基復(fù)合材料中的應(yīng)用[J];山西建筑;2005年24期

2 黃從運(yùn);王景春;;高強(qiáng)水泥基復(fù)合材料的研究[J];化學(xué)建材;1992年05期

3 孫偉;高性能水泥基復(fù)合材料的新進(jìn)展[J];港口工程;1995年01期

4 黃從運(yùn);高強(qiáng)水泥基復(fù)合材料[J];化學(xué)建材;1996年01期

5 石景星;水泥基復(fù)合材料科學(xué)與技術(shù)學(xué)術(shù)討論會(huì)在京隆重舉行[J];中國(guó)建材;1999年11期

6 余海燕,趙瑞霞,鄒輝峰;水泥基復(fù)合材料的發(fā)展與展望[J];河南建材;2005年03期

7 李民強(qiáng);;聚合物水泥基復(fù)合材料研究及進(jìn)展[J];廣東建材;2007年07期

8 王彩輝;孫偉;蔣金洋;孫國(guó)文;喬運(yùn)峰;;水泥基復(fù)合材料在多尺度方面的研究進(jìn)展[J];硅酸鹽學(xué)報(bào);2011年04期

9 鄒君;;蔗渣纖維增強(qiáng)水泥基復(fù)合材料的研究及發(fā)展前景[J];廣西輕工業(yè);2011年11期

10 陳恩義;談水泥基復(fù)合材料科學(xué)研究中的科學(xué)方法[J];中國(guó)建材;1993年07期

相關(guān)會(huì)議論文 前10條

1 張學(xué)旭;張書香;施強(qiáng);許仲梓;;聚合物-水泥基復(fù)合材料研究進(jìn)展[A];第九屆全國(guó)水泥和混凝土化學(xué)及應(yīng)用技術(shù)會(huì)議論文匯編（上卷）[C];2005年

2 江小平;黨秀英;譚一鳴;陳太林;;高性能纖維增強(qiáng)水泥基復(fù)合材料的制備、抗爆性能及發(fā)展趨勢(shì)[A];第十二屆全國(guó)結(jié)構(gòu)工程學(xué)術(shù)會(huì)議論文集第Ⅲ冊(cè)[C];2003年

3 郭垂根;韓福芹;邵博;王清文;;稻草增強(qiáng)水泥基復(fù)合材料的研究[A];第七屆全國(guó)纖維水泥制品學(xué)術(shù)、標(biāo)準(zhǔn)、技術(shù)信息經(jīng)驗(yàn)交流會(huì)暨第二屆三次中國(guó)硅酸鹽學(xué)會(huì)混凝土水泥制品分會(huì)纖維水泥制品專業(yè)委員會(huì)、第二屆二次中國(guó)硅酸鹽學(xué)會(huì)房建材料分會(huì)建筑結(jié)構(gòu)與輕質(zhì)板材專業(yè)委員會(huì)論文匯編[C];2008年

4 譚志催;李悅;霍達(dá);;碳纖維水泥基復(fù)合材料的應(yīng)用發(fā)展現(xiàn)狀[A];第三屆全國(guó)商品混凝土信息技術(shù)交流大會(huì)暨2006全國(guó)商品混凝土年會(huì)論文集[C];2006年

5 崔素萍;王林;;二氧化錳-水泥基復(fù)合材料的制備與性能[A];第十屆全國(guó)水泥和混凝土化學(xué)及應(yīng)用技術(shù)會(huì)議論文摘要集[C];2007年

6 馮竟竟;閻培渝;傅宇方;;高溫下水泥基復(fù)合材料孔隙特征試驗(yàn)研究[A];中國(guó)硅酸鹽學(xué)會(huì)水泥分會(huì)首屆學(xué)術(shù)年會(huì)論文集[C];2009年

7 徐世p，

本文編號(hào)：1431351