  本文選題：納米滲透 + HCC　； 參考：《新型建筑材料》2015年12期

【摘要】：研究了膠凝材料、高活性物質(zhì)、化學(xué)添加劑用量對HCC滲透型修補砂漿本體強度、粘結(jié)性能及其耐候性的影響,通過SEM分析了修補砂漿水化物在不同齡期的晶體生長過程,得出了HCC滲透型修補砂漿的最優(yōu)配比。試驗結(jié)果表明,按最優(yōu)配比制備的HCC滲透型修補砂漿具有很好的技術(shù)性能和施工性能,符合或優(yōu)于JG/T 336—2011《混凝土結(jié)構(gòu)修復(fù)用聚合物水泥砂漿》標(biāo)準(zhǔn)中A型的要求。
[Abstract]:The effects of cementitious materials, high active substances and chemical additives on the bulk strength, adhesive properties and weathering resistance of HCC permeable repair mortar were studied. The crystal growth process of repaired mortar hydrates at different ages was analyzed by SEM. The optimum ratio of HCC permeable repair mortar is obtained. The experimental results show that the HCC permeable repair mortar prepared with the optimal ratio has good technical and construction properties, which meets or is superior to the requirement of type A in the standard of JG/T 336-2011 "Polymer cement mortar for the repair of concrete structures".
【作者單位】： 南京滬聯(lián)新型建材有限公司;
【分類號】：TU578.1

【相似文獻】

相關(guān)期刊論文 前3條

1 王元曦;;水基滲透型無機防水劑的應(yīng)用現(xiàn)狀與前景[J];安徽建筑;2013年04期

2 朱國鋒;;路橋水性滲透型無機防水劑防水工程施工要點[J];黑龍江水利科技;2012年08期

3 ;[J];;年期

相關(guān)會議論文 前1條

1 沈春林;褚建軍;;國家行業(yè)標(biāo)準(zhǔn)建材《水性滲透型無機防水劑》(JCT1018—2006)解讀[A];全國第九次防水材料技術(shù)交流大會論文集[C];2007年

相關(guān)重要報紙文章 前1條

1 胡品;超滲透型防水劑[N];中國房地產(chǎn)報;2004年

，

本文編號：1964353