本文選題：生物彈性體 + 木糖醇　； 參考：《稀有金屬材料與工程》2014年S1期

【摘要】：將谷氨酸引入木糖醇類彈性體,以癸二酸、N-Boc谷氨酸和木糖醇為反應(yīng)單體,采用熔融縮聚法制備了新型氨基酸類彈性體(PXGS)。結(jié)果表明,該彈性體的玻璃化轉(zhuǎn)變溫度都低于室溫,能和人體組織、器官相匹配;其抗拉伸強(qiáng)度0.17~1.79 MPa、拉伸斷裂伸長率226%~972%;材料在pH=7.4的PBS溶液中降解,降解速度可通過改變單體配比調(diào)節(jié)。此外,彈性體吸水率不大,在水環(huán)境中具有較好的穩(wěn)定性且親水性能良好。所制備的PXGS制備過程較簡便,產(chǎn)物純凈,后處理簡單,有望在醫(yī)學(xué)領(lǐng)域用作引導(dǎo)組織修復(fù)的膜材料、組織工程支架、藥物緩釋載體等領(lǐng)域得到應(yīng)用。
[Abstract]:Glutamic acid was introduced into xylitol elastomer. A new amino acid elastomer, PXGSN, was prepared by melt Polycondensation with N-Boc glutamate and xylitol as reaction monomers. The results show that the glass transition temperature of the elastomer is lower than that of room temperature and can match human tissues and organs. The tensile strength of the elastomer is 0.17 ~ 1.79 MPa, the elongation at tensile break is 226 and 972. The material is degraded in the PBS solution of pH=7.4. The degradation rate can be adjusted by changing the monomer ratio. In addition, the elastomer has little water absorption, good stability and good hydrophilicity in water environment. The prepared PXGS has the advantages of simple preparation, pure product and simple post-treatment. It is expected to be used as membrane material for tissue repair, scaffold for tissue engineering, drug delivery carrier and so on in the field of medicine.
【作者單位】： 江南大學(xué);
【基金】：國家自然科學(xué)基金(51003042)
【分類號(hào)】：TQ334;R318.08

【共引文獻(xiàn)】

相關(guān)期刊論文 前1條

1 丁濤;任艷蓉;劉會(huì)芳;王穎;房曉敏;徐元清;;可生物降解聚蘋果酸-1,6-己二醇酯彈性體的合成與性能研究[J];鄭州師范教育;2013年06期

相關(guān)博士學(xué)位論文 前3條

1 王偉偉;環(huán)醚側(cè)基修飾的PCL/PEG嵌段共聚物可注射溫敏凝膠及腫瘤局部給藥的研究[D];天津大學(xué);2012年

2 周淑彥;葡聚糖基“智能”納米凝膠的自組裝輔助制備及生物應(yīng)用研究[D];上海交通大學(xué);2014年

3 張利;基于雙親縮肽嵌段共聚物納米粒的制備及其在藥物緩控釋研究中的應(yīng)用[D];天津大學(xué);2013年

相關(guān)碩士學(xué)位論文 前1條

1 龔云;側(cè)基功能化聚酯的合成與表征[D];東北師范大學(xué);2013年

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 劉全勇;吳s鷖，

本文編號(hào)：1947414