本文選題：半透性　切入點：透射率　出處：《華西口腔醫(yī)學(xué)雜志》2017年03期

【摘要】：目的研究牙科領(lǐng)域中透射率(T)、透射系數(shù)(TP)、對比系數(shù)(CR)3種常用半透性測量指標(biāo)的相互關(guān)系。方法制作Vita體瓷和釉瓷試件各6個,起始厚度為1.2 mm,逐漸打磨至1.0、0.8、0.6、0.4、0.2 mm,用PR-650型光譜掃描色度儀分別測量每個厚度下的T值、黑白背景前的顏色參數(shù)、黑白背景前的反射率,比較3種半透性測量指標(biāo)T、TP、CR的關(guān)系。結(jié)果 T與厚度之間呈指數(shù)關(guān)系,隨著厚度的減小T值明顯升高;TP值隨試件厚度減小而升高,接近于直線關(guān)系;CR值隨試件厚度減小而降低,接近于直線關(guān)系。不同厚度試件的T、TP、CR,除釉質(zhì)瓷1.2 mm組與1.0 mm組的T值無統(tǒng)計學(xué)差異外,其余各組結(jié)果之間均有統(tǒng)計學(xué)差異。3項指標(biāo)的變異系數(shù)(CV)無統(tǒng)計學(xué)差異。TP與T、CR與T之間均為指數(shù)關(guān)系,擬合優(yōu)度分別為0.951和0.939,具有統(tǒng)計學(xué)意義(P0.05)。結(jié)論在本實驗條件下,T、TP、CR這3種半透性的測量指標(biāo)具有相同的離散度,T與TP、T與CR均為指數(shù)關(guān)系,TP和CR的測量結(jié)果不能準(zhǔn)確地反映不同材料之間半透性差異的大小。
[Abstract]:Objective to study the relationship among three commonly used semi-permeable measurement indexes in the field of dentistry, I. e., transmissivity, transmission coefficient (TX), transmission coefficient (TP), and contrast coefficient (CR).Methods six samples of Vita body and six samples of glazed porcelain were made, the initial thickness was 1.2mm, and the thickness was gradually polished to 1.0mm 0.80.6U 0.40.2.The T value of each thickness, the color parameters before black and white background, and the reflectivity before black and white background were measured by PR-650 spectroscopic scanning colorimeter.To compare the relationship of three semi-permeability measurement indexes (TGTPN CR).Results there was an exponential relationship between T and thickness. With the decrease of thickness, the value of TP increased with the decrease of the thickness of the specimen, and the value of CR decreased with the decrease of the thickness of the specimen, and the value of CR was close to the linear relationship with the decrease of the thickness of the specimen.There was no significant difference in T value between the enamel porcelain 1.2 mm group and 1.0 mm group, but there was no significant difference in the coefficient of variation (CVV) between the other three groups. There was no significant difference between TP, TCR and T, and there was an exponential relationship between TP and Tncr and T.The goodness of fit was 0.951 and 0.939, respectively, with statistical significance (P 0.05).Conclusion under this experimental condition, the three semi-permeable indexes of TTP / TPN CR have the same dispersion degree T and TPN T and CR are exponential relationship. The measured results of TP and CR can not accurately reflect the difference of semi-permeability between different materials in this experiment. [WT5 "HZ] [WT5" HZ] [WT5 "BZ] the results of this experiment show that the three semi-permeable indexes have the same dispersion degree.
【作者單位】： 口腔疾病研究國家重點實驗室國家口腔疾病臨床研究中心四川大學(xué)華西口腔醫(yī)院修復(fù)科;口腔疾病研究國家重點實驗室國家口腔疾病臨床研究中心四川大學(xué)華西口腔醫(yī)院口腔頜面外科;
【基金】：四川省科技支撐計劃(2014FZ0073,2014SZ0019-8)~~
【分類號】：R783.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前9條

1 劉華;;氧化鋯含量對氧化鋯滲透陶瓷半透性的影響[J];吉林醫(yī)學(xué);2011年15期

2 黃伍旗;;氧化鋯含量對氧化鋯滲透陶瓷半透性的影響[J];武警醫(yī)學(xué)院學(xué)報;2011年08期

3 熊芳;巢永烈;朱智敏;;瓷層厚度比和瓷粉混合比對飾面瓷半透性的影響[J];實用口腔醫(yī)學(xué)雜志;2008年04期

4 熊芳,巢永烈;天然牙和牙科修復(fù)材料的半透性[J];國外醫(yī)學(xué).口腔醫(yī)學(xué)分冊;2005年06期

5 包廣潔;秦琨;康宏;沈利亞;劉名劍;;復(fù)合添加劑對氧化鋯增韌氧化鋁牙用陶瓷半透性的影響[J];中國組織工程研究與臨床康復(fù);2008年27期

6 孔凡玲;郭小文;朱洪水;;全瓷修復(fù)材料半透性研究[J];中國實用口腔科雜志;2009年06期

7 熊芳;朱智敏;巢永烈;;瓷層厚度對Vita飾面瓷顏色和半透性的影響[J];中華口腔醫(yī)學(xué)研究雜志(電子版);2008年01期

8 李玲;孫翔;高婧;李芳;沈麗娟;鄧再喜;陳吉華;;核瓷瓷層厚度對IPS e.max~汶Press核瓷顏色和半透性的影響[J];臨床口腔醫(yī)學(xué)雜志;2010年01期

9 ;[J];;年期

相關(guān)會議論文 前2條

1 孫翔;陳吉華;鄧再喜;;IPS e.max press全瓷系統(tǒng)瓷塊的色度學(xué)和半透性測定[A];2009“牙齒顏色的識別與美學(xué)再現(xiàn)”專題研討會論文匯編[C];2009年

2 巢永烈;熊芳;;天然牙和牙科陶瓷的半透性[A];2009“牙齒顏色的識別與美學(xué)再現(xiàn)”專題研討會論文匯編[C];2009年

相關(guān)博士學(xué)位論文 前1條

1 熊芳;天然牙和牙科陶瓷半透性的研究[D];四川大學(xué);2006年

相關(guān)碩士學(xué)位論文 前2條

1 李芷;切削及熱壓鑄造二硅酸鋰陶瓷的半透性及色彩研究[D];南京大學(xué);2016年

2 管紅雨;牙齦色瓷的半透性及色度學(xué)實驗研究[D];四川大學(xué);2007年

，

本文編號：1717511