本文選題：鐵　切入點：多巴胺　出處：《稀有金屬材料與工程》2014年S1期 　論文類型：期刊論文

【摘要】：為了提高可降解材料鐵的血液相容性,利用鹽酸多巴胺在堿性條件下能發(fā)生自發(fā)聚合的特性,對鐵表面進行了改性研究。由于聚多巴胺表面有活性反應(yīng)基團,從而可以將BSA(牛血清白蛋白)固載到鐵表面。利用FESEM、AFM、FTIR-ATR、接觸角測定、MTT實驗、溶血和血小板實驗等對鐵表面膜層的形貌、成分、親水性、細胞毒性和血液相容性進行了研究。結(jié)果表明,在鐵表面成功地修飾上了聚多巴胺BSA膜層,并且膜層沒有明顯的細胞毒性,能有效減少血小板的粘附。
[Abstract]:In order to improve the blood compatibility of degradable iron, the surface of iron was modified by the spontaneous polymerization of dopamine hydrochloride under alkaline conditions. In this way, BSA (bovine serum albumin) was immobilized on the surface of iron. The morphology, composition and hydrophilicity of the film on iron surface were determined by contact angle, MTT test, hemolysis and platelet test, using Fesemer AFMU FTIR-ATR. Cytotoxicity and blood compatibility were studied. The results showed that the polydopamine BSA film was successfully modified on the iron surface, and the membrane had no obvious cytotoxicity, which could effectively reduce the adhesion of platelets.
【作者單位】： 北京大學(xué);
【基金】：國家自然科學(xué)基金(31070846,30870623)
【分類號】：R318.08

【相似文獻】

相關(guān)期刊論文 前10條

1 潘長江,王進,黃楠,孫鴻,楊蘋,冷永祥,陳俊英,萬國江;等離子體表面接枝改性聚對苯二甲酸乙二醇酯的血液相容性研究[J];功能材料;2003年04期

2 吳玉厚,張善鋒,劉殿紅,李言秋,周國利;血液相容性材料研究進展[J];聊城大學(xué)學(xué)報(自然科學(xué)版);2003年02期

3 譚鴻,李潔華,謝興益,郭敏,傅強,鐘銀屏;含氟聚醚聚氨酯與聚醚聚氨酯共混的表面結(jié)構(gòu)及血液相容性的研究[J];生物醫(yī)學(xué)工程學(xué)雜志;2004年04期

4 魏文,程為莊;血液相容性及表面改性的研究[J];高分子通報;2004年05期

5 王琴梅,滕偉,潘仕榮,張靜夏;聚谷氨酸芐酯/聚乙二醇嵌段共聚物膜的血液相容性研究[J];生物醫(yī)學(xué)工程學(xué)雜志;2005年01期

6 浦鳴;計劍;李曉林;沈家驄;;水溶性梳狀聚乙二醇構(gòu)建的血液相容性涂層[J];高分子學(xué)報;2006年05期

7 歐陽晨曦;李沁;王維慈;周飛;徐衛(wèi)林;李文斌;;小口徑人工血管血液相容性[J];中國組織工程研究與臨床康復(fù);2008年06期

8 梅恒;胡豫;張治華;王華芳;郭濤;魏文寧;;二氧化鈦納米材料對家兔血液相容性影響[J];中國公共衛(wèi)生;2010年01期

9 習(xí)羽;賀春麗;楊桑;朱皓淼;黃小波;李利;周寧琳;章峻;沈健;;聚乙烯表面親水化改性及其血液相容性改進[J];功能材料;2011年08期

10 伏鵬;劉成s，

本文編號：1628133