本文選題：聚氨酯　切入點(diǎn)：熱致相分離　出處：《稀有金屬材料與工程》2014年S1期 　論文類(lèi)型：期刊論文

【摘要】：以分子量為2000的聚己內(nèi)酯(PCL)作為軟段,六亞甲基二異氰酸酯(HMDI)作為硬段,分子量為250的聚四氫呋喃(PTMG)為擴(kuò)鏈劑,通過(guò)調(diào)整不同軟硬段的比例,合成了5組具有不同特性的可降解聚氨酯材料,并對(duì)相應(yīng)的聚氨酯的分子量、力學(xué)性能、熱性能等進(jìn)行了研究,同時(shí)以不同特性的PU為基礎(chǔ),構(gòu)建出了具有多力學(xué)層區(qū)結(jié)構(gòu)的多孔軟骨組織工程支架,并對(duì)其孔隙結(jié)構(gòu)進(jìn)行了分析。
[Abstract]:The polycaprolactone (PCL) with molecular weight of 2000 was used as soft segment, hexamethylene diisocyanate (HMDI) as hard segment and polytetrahydrofuran (PTMGG) with molecular weight 250 as chain extender. By adjusting the ratio of different soft and hard segments, Five groups of degradable polyurethane materials with different properties were synthesized, and their molecular weight, mechanical properties and thermal properties were studied. The porous cartilage tissue engineering scaffold with multi-layer structure was constructed and its pore structure was analyzed.
【作者單位】： 華南理工大學(xué);國(guó)家人體組織功能重建工程技術(shù)研究中心;
【基金】：教育部新世紀(jì)優(yōu)秀人才支持計(jì)劃項(xiàng)目(NCET-12-0200) 廣州市科技計(jì)劃項(xiàng)目(2012J4100124)
【分類(lèi)號(hào)】：O631.3;R318.08

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 Ni-jia Song;Xia Jiang;Jie-hua Li;Yong Pang;Jian-shu Li;Hong Tan;Qiang Fu;;THE DEGRADATION AND BIOCOMPATIBILITY OF WATERBORNE BIODEGRADABLE POLYURETHANES FOR TISSUE ENGINEERING[J];Chinese Journal of Polymer Science;2013年10期

2 王芋驍;孔志杰;黃溪;馬林;;交聯(lián)改性絲素蛋白材料制備和醫(yī)學(xué)應(yīng)用[J];現(xiàn)代絲綢科學(xué)與技術(shù);2013年05期

3 郭立強(qiáng);;聚乳酸-羥基乙酸共聚物的研究進(jìn)展[J];化工技術(shù)與開(kāi)發(fā);2014年05期

4 黎慶安;范昌平;;水性聚氨酯層壓膠的制備及性能[J];廣東化工;2014年15期

5 李新s，

本文編號(hào)：1573564