本文關鍵詞： 快速熱循環(huán)注塑 注塑工藝 模具設計 汽車內飾　出處：《湖北工業(yè)大學》2017年碩士論文　論文類型：學位論文

【摘要】：快速熱循環(huán)注塑成型技術便是其中備受關注的新型綠色注塑成型技術之一。與常規(guī)注塑不同,快速熱循環(huán)注塑成型技術工藝是在模具型腔表面溫度略高于成型樹脂的玻璃化轉變溫度時對樹脂進行充型的一種注塑工藝,并在高溫保持后實現(xiàn)產(chǎn)品的快速冷卻,以此改善塑料制品的表面質量,避免二次加工工藝,減少對環(huán)境及操作人員的危害。重點闡述了快速熱循環(huán)注塑成型技術,探究了快速熱循環(huán)注塑成型工藝,并對實驗結果進行了討論,結果表明在快速熱循環(huán)注塑成型中各工藝參數(shù)對熔體流動性影響程度大小依次為:型腔表面溫度型腔高度注射速度熔體溫度。簡要介紹了某汽車內飾產(chǎn)品的基本情況,分析了某汽車內飾產(chǎn)品快速熱循環(huán)模具的設計流程,并對其進行了快速熱循環(huán)模具設計;設計了相關實驗對其進行驗證,并詳細的闡述了試驗原料和吹塑參數(shù)、模具響應評估、試驗結果與討論。建立了注塑成型的充填過程和翹曲變形過程的數(shù)學模型,并簡要介紹了Moldflow軟件以及基于Moldflow的數(shù)值分析流程;重點對某汽車內飾產(chǎn)品進行了數(shù)值分析,包括Moldflow前處理、熱流道澆注系統(tǒng)的創(chuàng)建、分析類型及工藝參數(shù)的設置并完成了數(shù)值分析;設計了正交實驗;分析了工藝參數(shù)對翹曲的影響,并對其工藝參數(shù)進行優(yōu)化。
[Abstract]:The rapid thermal cycle injection molding technology is one of the new green injection molding technologies which has attracted much attention. It is different from the conventional injection molding technology. Rapid thermal cycle injection molding technology is a kind of injection molding technology when the surface temperature of mold cavity is slightly higher than the glass transition temperature of molding resin. In order to improve the surface quality of plastic products and avoid the secondary processing process, the rapid cooling of the products is realized after the high temperature maintenance. In order to reduce the harm to the environment and operators, the technology of rapid thermal cycle injection molding is expounded, the technology of rapid thermal circulation injection molding is explored, and the experimental results are discussed. The results show that in the rapid thermal cycle injection molding, the influence of each process parameter on the melt fluidity is as follows:. Cavity surface temperature cavity height injection velocity melt temperature. The basic situation of a car interior decoration product is briefly introduced. This paper analyzes the design flow of the rapid heat circulation mould for a certain automobile interior decoration product, and designs the rapid heat circulation mould for it. Related experiments were designed to verify it, and the test materials and blow molding parameters, mold response evaluation were described in detail. The mathematical models of filling process and warping process of injection molding are established, and the Moldflow software and the numerical analysis flow based on Moldflow are introduced briefly. The numerical analysis of an automobile interior decoration product was carried out, including Moldflow pretreatment, the establishment of hot runner gating system, the setting up of analysis type and process parameters, and the numerical analysis. The orthogonal experiment is designed. The effect of process parameters on warpage was analyzed and optimized.
【學位授予單位】：湖北工業(yè)大學
【學位級別】：碩士
【學位授予年份】：2017
【分類號】：TQ320.662;U463.839.2

【參考文獻】

相關期刊論文 前10條

1 周長長;柳和生;賴家美;黃興元;熊愛華;何建濤;;工藝參數(shù)對短玻纖增強聚丙烯氣輔注塑成型的影響[J];塑料工業(yè);2013年10期

2 王祖明;于滬平;尹紅靈;夏松穎;;基于外置式感應加熱的注塑缺陷模擬及實驗研究[J];工程塑料應用;2012年03期

3 劉東雷;申長雨;劉春太;辛勇;孫玲;伍曉宇;;基于響應曲面法與改進遺傳算法的RHCM成型工藝優(yōu)化[J];機械工程學報;2011年14期

4 陳晨;劉全坤;王成勇;易學滿;;高光液晶前殼翹曲變形分析與工藝參數(shù)智能優(yōu)化[J];塑性工程學報;2011年02期

5 丁立波;;提高氣輔成型制品質量關鍵技術的研究[J];塑料工業(yè);2010年12期

6 王桂龍;趙國群;李輝平;管延錦;;基于CAE的大型LCD注塑面板變模溫設計與分析[J];材料工程;2009年09期

7 王桂龍;趙國群;李輝平;管延錦;;蒸氣輔助快速熱循環(huán)注塑技術及模溫響應模擬[J];高分子材料科學與工程;2009年08期

8 張愛敏;趙國群;高軍;陳國文;嚴柳青;;基于快速熱循環(huán)注塑工藝要求的ABS改性[J];合成樹脂及塑料;2009年02期

9 趙國群;王桂龍;李輝平;管延錦;;快速熱循環(huán)注塑技術的研究與應用[J];塑性工程學報;2009年01期

10 李熹平;趙國群;管延錦;李輝平;;快速熱循環(huán)注塑模具加熱與冷卻過程分析及其結構優(yōu)化設計[J];塑性工程學報;2009年01期

相關博士學位論文 前6條

1 肖成龍;電熱式快速熱循環(huán)成型關鍵技術研發(fā)及機理分析[D];華南理工大學;2015年

2 王偉華;快速熱循環(huán)注塑材料PC/ABS與PP的物理改性及其性能研究[D];山東大學;2015年

3 王小新;快速熱循環(huán)高光注塑模具加熱冷卻方法與產(chǎn)品質量控制技術研究[D];山東大學;2014年

4 劉繼濤;快速熱循環(huán)注塑成型過程數(shù)值模擬方法研究[D];山東大學;2011年

5 王桂龍;快速熱循環(huán)注塑成型關鍵技術研究與應用[D];山東大學;2011年

6 李熹平;快速熱循環(huán)注塑模具及工藝關鍵技術研究[D];山東大學;2010年

，

本文編號：1492482