【摘要】：對(duì)有機(jī)溶劑堿催化蒸煮處理后的絲瓜絡(luò)進(jìn)行堿抽提、二氧化氯漂白和過氧化氫多段漂白。討論了漂白過程中ClO_2和H_2O_2用量對(duì)漂白效果的影響。結(jié)果表明,當(dāng)ClO_2用量為3%、H_2O_2用量為5%時(shí),配合0.3%的MgSO_4和0.3%的Na_2SiO_3,在浴比為1∶9的條件下對(duì)樣品進(jìn)行漂白,得到的絲瓜絡(luò)溶解漿漿粕的卡伯值達(dá)到較低水平,蒸煮后纖維表面附著物減少,木質(zhì)素完全脫除。
[Abstract]:Alkali extraction, chlorine dioxide bleaching and hydrogen peroxide multistage bleaching were carried out on the luffa complex treated by alkali-catalyzed cooking with organic solvent. The effects of the dosage of ClO_2 and H_2O_2 on the bleaching effect were discussed. The results showed that when the dosage of ClO_2 was 3 / 10 / s / s, the samples were bleached with 0.3% MgSO_4 and 0.3% Na_2SiO_3, under the condition of 1:9 bath ratio. The kappa number of luffa complex dissolved pulp was lower than that of other pulp, the surface attachment was decreased and lignin was completely removed after cooking.
【作者單位】： 中原工學(xué)院;
【分類號(hào)】：TS192.56

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 薛軍岳 ,薛運(yùn)書;絲瓜——全身是寶[J];中國(guó)食品;1986年09期

2 王迎;沈新元;鄒曉蕾;;絲瓜絡(luò)纖維染色動(dòng)力學(xué)研究[J];印染助劑;2011年05期

3 弓太生;李玲;萬(wàn)蓬勃;;絲瓜絡(luò)纖維在鞋墊中的應(yīng)用及分析[J];皮革科學(xué)與工程;2013年01期

4 ;絲瓜絡(luò)鞋墊[J];小學(xué)自然教學(xué);1996年03期

5 肖燕;;掘金路上,一條絲瓜的“花樣年華”[J];女性天地;2012年03期

6 姬學(xué)亮,高安全,景中建;降低絲瓜絡(luò)油脂殘留量的研究[J];日用化學(xué)工業(yè);2004年03期

7 耿耘;馮華;蔣合眾;羅麗勤;馬超英;;冠脈通中絲瓜絡(luò)的提取工藝研究[J];上海中醫(yī)藥雜志;2007年02期

8 程醉;;猶抱琵琶半遮面,絲瓜纖維制品袍笏登場(chǎng)[J];中國(guó)纖檢;2010年14期

9 李紅;王迎;契丹寧;;絲瓜絡(luò)纖維的預(yù)處理實(shí)踐[J];上海紡織科技;2012年05期

10 好好;;絲瓜[J];啟蒙(0-3歲);2009年09期

相關(guān)會(huì)議論文 前2條

1 戴大臨;文藝;許禾聲;孫敏;張治中;;絲瓜絡(luò)中無機(jī)元素的EDS分析[A];2006年全國(guó)電子顯微學(xué)會(huì)議論文集[C];2006年

2 楊紅;陸強(qiáng);冉明浩;張夏聰;房Z，

本文編號(hào)：2301715