【摘要】：討論了LiF-NaF-KF-K_2TiF_6體系和CaCl_2-TiO_2熔鹽體系中的鈦離子還原機(jī)理的研究進(jìn)展。論述了KCl-Na Cl-K_2TiF_6體系、LiF-NaF-KF-K_2TiF_6體系、KCl-NaCl-KF-TiCl_3體系和KCl-Na Cl-TiCl_2體系的電沉積鈦金屬層的方法以及鈦離子在陰極的還原機(jī)理和沉積過程參數(shù)對(duì)鍍層性能的影響。介紹了NaCl-TiCl_2熔鹽體系電流接觸沉積法制備鐵鈦合金以及在泡沫碳表面電沉積鈦鉻合金的工藝。表明了熔鹽電沉積金屬鈦鍍層的可行性,并提出該工藝中需要解決的理論和應(yīng)用問題。
[Abstract]:The research progress of titanium ion reduction mechanism in LiF-NaF-KF-K_2TiF_6 system and CaCl_2-TiO_2 molten salt system is discussed.The method of electrodeposition of titanium metal layer in KCl-NaCl-KF-TiCl3 system and KCl-Na Cl-TiCl_2 system in LiF-NaF-KF-K2TiFST-6 system of KCl-Na Cl-K_2TiF_6 system is discussed. The reduction mechanism of titanium ion at cathode and the effect of deposition process parameters on the properties of the coating are discussed.The preparation process of Fe-Ti alloy by NaCl-TiCl_2 molten salt current contact deposition method and the process of electrodeposition of Ti-Cr alloy on the surface of foam carbon were introduced.The feasibility of molten salt electrodeposition of titanium coating is indicated, and the theoretical and practical problems need to be solved in this process are put forward.
【作者單位】： 華北理工大學(xué)冶金與能源學(xué)院現(xiàn)代冶金技術(shù)教育部重點(diǎn)實(shí)驗(yàn)室;
【基金】：國家自然科學(xué)基金(51474093) 河北省自然科學(xué)基金(E2016209163)
【分類號(hào)】：TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 ;用于高裝飾精飾電沉積銠[J];材料保護(hù);1999年10期

2 徐秉森 ,劉殿生 ,宋方考;電沉積制備天然，

本文編號(hào)：1756010