本文選題：高鋁粉煤灰　切入點(diǎn)：晶種分解　出處：《有色金屬(冶煉部分)》2016年08期

【摘要】：以高鋁粉煤灰熟料經(jīng)預(yù)脫硅—堿石灰燒結(jié)、溶出、二次脫硅后溶液為原料,通過晶種分解后生產(chǎn)擬薄水鋁石產(chǎn)品,考察了種分條件對(duì)擬薄水鋁石產(chǎn)品的影響,并對(duì)其進(jìn)行表征。結(jié)果表明,種分法制備的擬薄水鋁石產(chǎn)品孔容可達(dá)到0.829 1cm3/g,BET比表面積高達(dá)393.00m2/g,達(dá)到并優(yōu)于普通大孔擬薄水鋁石的理化指標(biāo),從而可實(shí)現(xiàn)高鋁粉煤灰中鋁資源的高附加值利用。
[Abstract]:The pseudo-boehmite product was produced from high-alumina fly ash clinker by pre-desilication alkali lime sintering dissolution and secondary desilication as raw material. The effect of seed separation conditions on pseudo-boehmite product was investigated and characterized.The results show that the pore volume of pseudo-boehmite prepared by seed separation method can reach 0.829 cm ~ (3) / g ~ (-1) BET specific surface area up to 393.00 m ~ (2 / g), which reaches and is superior to the physical and chemical index of ordinary large pore pseudo-boehmite, thus realizing the high added value utilization of aluminum resources in high-alumina fly ash.
【作者單位】： 東北大學(xué)多金屬共生礦生態(tài)化利用教育部重點(diǎn)實(shí)驗(yàn)室;
【基金】：國家自然科學(xué)基金資助項(xiàng)目(U1202274) 中央高�；究蒲袠I(yè)務(wù)費(fèi)專項(xiàng)資金項(xiàng)目(N140203005,N140204015) 中國博士后科學(xué)基金項(xiàng)目(2015M581352)
【分類號(hào)】：TF821;TQ536.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前6條

1 曾雙親;楊清河;肖成武;余波;;干燥方式及老化條件對(duì)擬薄水鋁石性質(zhì)的影響[J];石油煉制與化工;2012年06期

2 趙傳鴻;擬薄水鋁石膠溶性能的研究及打漿貯存應(yīng)用[J];齊魯石油化工;2005年04期

3 張孔遠(yuǎn);韓紅亮;周然然;燕京;;磷改性擬薄水鋁石性能及在蠟油加氫催化劑中的應(yīng)用[J];工業(yè)催化;2010年02期

4 李雪禮;婁來銀;譚爭(zhēng)國;張海濤;段宏昌;李荻;潘志爽;高雄厚;;擬薄水鋁石的性質(zhì)及其在催化裂化催化劑中的應(yīng)用[J];石化技術(shù)與應(yīng)用;2014年01期

5 申明樂;;利用PS鋁基材版酸洗堿洗處理廢液制備擬薄水鋁石[J];環(huán)境工程學(xué)報(bào);2010年11期

6 ;[J];;年期

相關(guān)碩士學(xué)位論文 前1條

1 徐登清;大孔擬薄水鋁石制備及加氫脫氧的研究[D];曲阜師范大學(xué);2011年

，

本文編號(hào)：1712775