本文選題：環(huán)氧樹脂　切入點：梯度交聯(lián)聚合物　出處：《高�；瘜W(xué)工程學(xué)報》2016年03期 　論文類型：期刊論文

【摘要】：以二氨基二苯甲烷(DDM)、D400和環(huán)氧樹脂(E44)為原料,通過疊層法制備了梯度交聯(lián)聚合物材料。用掃描電鏡、拉力試驗機和高級擴展流變儀研究了固化劑組份對制備的梯度交聯(lián)聚合物材料結(jié)構(gòu)、力學(xué)性能和阻尼性能的影響規(guī)律。結(jié)果表明,調(diào)整單層聚合物的交聯(lián)密度可得到用于不同使用溫度范圍的寬玻璃化轉(zhuǎn)變溫度,且力學(xué)性能優(yōu)異的無微相分離結(jié)構(gòu)梯度交聯(lián)聚合物材料。梯度交聯(lián)聚合物的玻璃化轉(zhuǎn)變溫度范圍最大可達130℃且峰值半高寬為81℃,有效阻尼溫域(tanδ0.3)為61.57℃,處于中溫溫度范圍內(nèi)。
[Abstract]:Gradient crosslinked polymer materials were prepared by lamination method using diaminodiphenylmethane (D400) and epoxy resin (E44) as raw materials. The effects of curing agent composition on the structure, mechanical properties and damping properties of gradient crosslinked polymer materials prepared by tensile force tester and advanced spreading rheometer were studied. The wide glass transition temperature can be obtained by adjusting the crosslinking density of monolayer polymers. The glass transition temperature range of gradient crosslinked polymer is up to 130 鈩，