【摘要】：分別對(duì)甲基苯基混合環(huán)體體系、八苯基環(huán)體體系通過(guò)開環(huán)聚合所制備的高黏度苯甲基硅油性能進(jìn)行了研究。結(jié)果表明,隨著封端劑用量的增加,苯甲基硅油的黏度降低,封端劑的合理使用能有效控制苯甲基硅油的黏度;隨著八甲基環(huán)四硅氧烷(D4)用量的增加,苯甲基硅油的折光率下降。由八苯基環(huán)體體系制備出的苯甲基硅油黏度受溫度的影響小于混合環(huán)體體系,耐熱性在質(zhì)量損失率為10%時(shí)優(yōu)于混合環(huán)體體系。
[Abstract]:The properties of high viscosity benzyl silicone oil prepared by ring-opening polymerization of methyl phenyl mixed ring system and octaphenyl ring system were studied respectively. The results showed that the viscosity of benzene methyl silicone oil decreased with the increase of the content of entrapment agent. The reasonable use of the entrapment can effectively control the viscosity of phenylmethyl silicone oil, and with the increase of octomethylcyclotetrasiloxane (D4) content, The viscosity of benzyl silicone oil prepared from octaphenyl ring system is less affected by temperature than that of mixed ring system, and the heat resistance is better than that of mixed ring system when the mass loss rate is 10.
【作者單位】： 上海應(yīng)用技術(shù)大學(xué)材料科學(xué)與工程學(xué)院;上海樹脂廠有限公司;
【基金】：上海市科促會(huì)/教育基金會(huì)聯(lián)盟計(jì)劃(LM201518) 上海應(yīng)用技術(shù)學(xué)院復(fù)合材料學(xué)科建設(shè)項(xiàng)目(10210Q150001)
【分類號(hào)】：TQ324.21

【相似文獻(xiàn)】

相關(guān)期刊論文 前3條

1 劉其昶;萬(wàn)榮根;王友功;常憲民;;苯甲基硅油損耗機(jī)理的研究(摘要)[J];絕緣材料通訊;1987年05期

2 蔣元椿;;國(guó)內(nèi)外苯甲基硅油、硅樹脂的生產(chǎn)應(yīng)用情況[J];杭州化工;1988年01期

3 李偉,陳曦,胡耿源;苯甲基硅油的合成及表征——IR、UV、NMR、VPO法[J];精細(xì)化工;1990年06期

，

本文編號(hào)：1611524