本文選題：廣西上林 + 銅鼓��； 參考：《文物保護與考古科學》2017年02期

【摘要】：為配合保護修復的需要,利用金相顯微鏡、掃描電鏡能譜儀對廣西上林縣館藏6面東漢至南朝時期的冷水沖型銅鼓進行了科技分析。結(jié)果表明,這6面銅鼓均為銅錫鉛三元合金組成,且為鑄造成型,其工藝利用泥范法和失蠟法相結(jié)合的方法。由于冷水沖型銅鼓的合金成分和鑄造工藝研究尚未見報道,因此,本研究分析數(shù)據(jù)為更深入研究冷水沖型銅鼓的科技內(nèi)涵提供了重要參考。
[Abstract]:In order to meet the need of protection and restoration, the cold water pounding copper drum collected in Shanglin County, Guangxi Province, was analyzed by means of metallographic microscope and scanning electron microscope (SEM) in the period from the Eastern Han Dynasty to the Southern Dynasty. The results show that the six copper drums are composed of copper, tin and lead ternary alloys, and are cast. The process is combined with mud method and wax loss method. Because the alloy composition and casting technology of cold water impact type copper drum have not been reported, the data of this study provide an important reference for further research on the scientific and technological connotation of cold water impact type copper drum.
【作者單位】： 復旦大學文物與博物館學系;廣西民族大學民族學與社會學學院科技史系;中國科學技術大學科技考古實驗室;
【基金】：“三區(qū)”人才支持計劃文化工作者專項資助(桂文發(fā)[2013]77號) 廣西高校科學技術研究項目資助(YB2014093)
【分類號】：K876.41

【參考文獻】

相關期刊論文 前10條

1 劉艷英;臧金旺;李憲武;;金相試樣制備過程概述[J];金屬世界;2010年01期

2 孫淑云;姚智輝;萬輔彬;;越南銅鼓及相關器物金相分析[J];桂林工學院學報;2005年04期

3 張利潔,趙福生,孫淑云,殷瑋璋;北京琉璃河燕國墓地出土銅器的成分和金相研究[J];文物;2005年06期

4 姚智輝,孫淑云,鄒后曦,方剛,黃偉,白彬,張建華;峽江地區(qū)部分青銅器的成分與金相研究[J];自然科學史研究;2005年02期

5 韓汝玢,孫淑云,李秀輝,潛偉;中國古代銅器的顯微組織[J];北京科技大學學報;2002年02期

6 吳坤儀;中國古代鑄造技術史略[J];哈爾濱工業(yè)大學學報(社會科學版);2001年04期

7 蔣廷瑜;銅鼓研究一世紀[J];民族研究;2000年01期

8 萬輔彬,李世紅,蔣廷瑜,邱鐘侖,韋顯初,農(nóng)學堅,華覺明,楊年,凌越,譚德睿,徐惠康;世界銅鼓之王──北流型101號銅鼓鑄造工藝研究[J];文物保護與考古科學;1995年01期

9 DavidA.Scott,賈瑩;古代金屬的微觀組織[J];文物保護與考古科學;1995年01期

10 吳來明;;“六齊”、商周青銅器化學成分及其演變的研究[J];文物;1986年11期

【共引文獻】

相關期刊論文 前10條

1 李冰潔;江旭東;潘春旭;;銅錫青銅合金腐蝕過程中的電化學與微結(jié)構(gòu)特征研究[J];材料導報;2017年11期

2 黃獻源;汪常明;金正耀;;廣西上林縣館藏東漢至南朝銅鼓科技分析研究[J];文物保護與考古科學;2017年02期

3 李建西;;(\∪，

本文編號：2056434