本文選題：青銅 + 大氣腐蝕��； 參考：《華東理工大學》2015年碩士論文

【摘要】：青銅文物是我國重要的歷史文化遺產,且具有不可再生性,對其保護具有非常重要的意義,而青銅文物的保存空間博物館展柜內的污染性氣體、光照、溫濕度都對青銅文物的保存有著嚴重的危害。因此,研究青銅在大氣環(huán)境中的腐蝕行為與規(guī)律是具有重要的理論價值與現實意義。本文主要采用QCM反應性監(jiān)測方法對表面鍍銅錫合金的石英晶振片在S02、NO2及其混合氣氛以及在博物館模擬展柜內的大氣腐蝕行為進行了原位監(jiān)測,得到了腐蝕動力學曲線,并聯合掃描電子顯微鏡(SEM)、能譜儀(EDS)、光電子能譜(XPS)分析手段對晶振片表面的腐蝕產物進行了分析,并初步推測了青銅文物模擬材料的大氣腐蝕機理。研究結果表明,NO2、NO2均能加速青銅文物模擬材料的大氣腐蝕,且兩者存在時具有協同效應。升高NO2、NO2氣體濃度與反應溫度都會不同程度地加快青銅文物模擬材料的腐蝕速度。光照的存在以及溫濕度的升高都會加速青銅文物模擬材料的腐蝕,其中傲特盛鹵素燈對青銅文物模擬材料腐蝕影響最嚴重,在色溫較高時對青銅文物模擬材料的腐蝕更為嚴重。青銅文物模擬材料在光照條件下腐蝕60天后的主要腐蝕產物為Cu2O、CuO、SnO、SnO2,其次還有銅的硫酸鹽、銅的硝酸鹽、銅的碳酸鹽、銅的硫化物以及銅的氯化物。
[Abstract]:Bronze cultural relic is an important historical and cultural heritage of our country, and it is not renewable, it has very important significance for its protection, and the preservation space of bronze cultural relic is polluted gas and illumination in the exhibition cabinet of museum. Temperature and humidity are serious harm to the preservation of bronze relics. Therefore, it is of great theoretical and practical significance to study the corrosion behavior and law of bronze in atmospheric environment. In this paper, QCM reactivity monitoring method is used to monitor in situ the corrosion behavior of quartz crystal wafer on the surface of copper-tin alloy in S02NO2 and its mixed atmosphere, as well as the atmospheric corrosion behavior in the museum simulated display cabinet, and the corrosion kinetics curves are obtained. The corrosion products on the surface of the wafer were analyzed by means of scanning electron microscope (SEM), energy spectrometer (EDS) and photoelectron spectroscopy (XPS), and the atmospheric corrosion mechanism of the simulated material of bronze cultural relic was preliminarily speculated. The results show that no _ 2O _ 2 can accelerate the atmospheric corrosion of bronze cultural relic simulation materials, and they have synergistic effect when they exist. Increasing the concentration of no _ 2O _ 2 gas and reaction temperature can accelerate the corrosion rate of bronze antiquities. The existence of light and the increase of temperature and humidity will accelerate the corrosion of bronze cultural relic simulation material, among which, the corrosion of bronze cultural relic simulative material is most serious by Aotesian halogen lamp, and the corrosion of bronze cultural relic simulation material is more serious when the color temperature is higher. The main corrosion products of bronze cultural relic simulation material after 60 days of corrosion under illumination are Cu _ 2O _ 2, Cu _ 2O _ (CuO), Sno _ (2) O _ (2), copper sulfate, copper nitrate, copper carbonate, copper sulfide and copper chloride.
【學位授予單位】：華東理工大學
【學位級別】：碩士
【學位授予年份】：2015
【分類號】：K876.41

【參考文獻】

相關期刊論文 前10條

1 胡星明;畢建洪;;青銅文物腐蝕與保護研究[J];安徽大學學報(自然科學版);2007年04期

2 張允誠;置換鍍銅-錫合金替代氰化物預鍍銅工藝的探討[J];電鍍與精飾;2002年05期

3 于國才,王振堯,陳鴻川;沈陽地區(qū)碳鋼、耐候鋼的腐蝕規(guī)律研究[J];腐蝕與防護;2000年06期

4 王鳳平,嚴川偉,張學元,杜元龍;石英晶體微天平(QCM)及其在大氣腐蝕研究中的應用[J];化學通報;2001年06期

5 鄭傳波;黃彥良;朱永艷;李言濤;;金屬大氣腐蝕實驗方法進展與研究動態(tài)[J];海洋科學;2005年11期

6 劉云;林雪燕;;銅金屬經過SO_2腐蝕后的腐蝕物特性[J];機電元件;2008年01期

7 安百剛;張學元;韓恩厚;;沈陽大氣環(huán)境下純銅的初期腐蝕行為[J];金屬學報;2007年01期

8 王鳳平,嚴川偉,張學元,閆一功,杜元龍;石英晶體微天平研究Zn在薄液膜下的腐蝕動力學[J];物理化學學報;2001年04期

9 周浩,祝鴻范,蔡蘭坤;青銅器銹蝕結構組成及形態(tài)的比較研究[J];文物保護與考古科學;2005年03期

10 王振堯，鄭逸蘋，，劉壽榮;A3鋼在人造污染介質中的大氣腐蝕行為[J];中國腐蝕與防護學報;1994年03期

相關會議論文 前1條

1 康蘇花;竇紅;;臭氧及其在各行業(yè)的應用簡述[A];河北省土壤污染防治技術研討會論文集[C];2010年

本文編號：1841397