【摘要】：本文利用金相顯微鏡和掃描電鏡能譜儀對(duì)湖北隨州葉家山西周墓地M65出土的42件青銅器進(jìn)行了金相實(shí)驗(yàn)研究,結(jié)果表明其中的31件材質(zhì)為鉛錫青銅,10件為錫青銅,僅有1件為鉛青銅;銅器制作主要采用鑄造工藝,僅個(gè)別兵器在局部進(jìn)行了熱鍛加工;具有相同銘文、紋飾風(fēng)格一致的銅容器的合金成分、金相組織和鑄造技術(shù)等方面也較為一致。這些結(jié)果為研究M65出土青銅器的生產(chǎn)組織問(wèn)題提供科學(xué)資料。
[Abstract]:In this paper, a metallographic study was carried out on 42 bronzes unearthed from M65 in Shanxi Province Cemetery of Suizhou, Hubei Province by means of metallographic microscope and scanning electron microscope. The results showed that 31 of them were made of lead-tin bronze and 10 were tin bronze.Only one piece is lead bronze; copper ware is made mainly by casting, and only a few weapons are hot-forged locally; the alloy composition of copper containers with the same inscription and pattern is identical.Metallographic structure and casting technology are also more consistent.These results provide scientific data for the study of the production organization of bronzes unearthed in M 65.
【作者單位】： 北京科技大學(xué)冶金與材料史研究所;中國(guó)社會(huì)科學(xué)院考古研究所;湖北省文物考古研究所;北京大學(xué)考古文博學(xué)院;
【分類號(hào)】：K876.41

【參考文獻(xiàn)】

相關(guān)期刊論文 前5條

1 劉靜;;先秦時(shí)期青銅鉞的再研究[J];故宮博物院院刊;2007年02期

2 林l，

本文編號(hào)：1732572