本文關(guān)鍵詞：新型MRI對比劑釓噴酸摻雜的介孔二氧化硅納米粒的制備、表征及MR成像　出處：《重慶醫(yī)科大學(xué)》2017年碩士論文　論文類型：學(xué)位論文

  更多相關(guān)文章： 介孔二氧化硅 釓噴酸 納米材料 磁共振成像 對比劑

【摘要】：目的研制一種新型的具有分子靶向顯像潛能的高摻釓量的介孔二氧化硅納米粒子用于磁共振成像。方法采用反向微乳液法將釓噴酸(Gadopentetic acid,GA)加入到微乳液體系中,從而將GA摻雜到介孔二氧化硅(mesoporous silica nanoparticles,MSN)的孔道中,制備出摻雜GA的二氧化硅納米材料(Gd-MSN);同時制備不含釓的MSN為對照。用馬爾文粒度儀、透射電鏡(Transmission electron microscope,TEM)觀察納米粒的粒徑及形貌特征;電感耦合等離子體原子發(fā)射光譜分析(Inductively Coupled Plasma-Atomic Emission Spectrometry,ICP-AES)檢測納米粒的含釓量和穩(wěn)定性;CCK-8(Cell Counting Kit-8,CCK-8)法檢測納米粒的細(xì)胞毒性;最后用3.0T磁共振成像系統(tǒng)觀察納米粒的體內(nèi)外磁共振成像效果。結(jié)果成功制備出釓噴酸摻雜的二氧化硅納米材料Gd-MSN,TEM觀察Gd-MSN形態(tài)呈圓球形,馬爾文測得其平均粒徑約105-128nm;ICP-AES測得摻釓量最高可達(dá)771.08μmo L/g,Gd-MSN在體外環(huán)境中具有良好的穩(wěn)定性,且在25,50,100μg/m L的濃度下沒有明顯的細(xì)胞毒性;體內(nèi)外磁共振結(jié)果顯示Gd-MSN能顯著縮短T1和T2的弛豫時間,表現(xiàn)為短T1短T2的信號特點(diǎn)。結(jié)論成功制備了單分散、易修飾、高載藥量的新型摻釓納米材料,有望成為一種新型的多功能靶向磁共振納米對比劑。
[Abstract]:Objective to develop a new type of molecular targeted high amount of potential imaging gadolinium doped mesoporous silica nanoparticles for magnetic resonance imaging. Methods using reverse microemulsion method gadopentetic acid (Gadopentetic acid, GA) added to the micro emulsion system, thus to the GA doped mesoporous silica (mesoporous silica, nanoparticles, MSN) in the channels of the prepared silica nanomaterials doped with GA (Gd-MSN); at the same time preparing gadolinium containing MSN as control. Using the Malvin particle analyzer, transmission electron microscopy (Transmission electron, microscope, TEM) to observe the nanoparticles size and morphology; inductively coupled plasma atomic emission spectrometry (Inductively Coupled Plasma-Atomic Emission Spectrometry, ICP-AES) gadolinium content and stability were detected; CCK-8 (Cell Counting Kit-8 CCK-8) method was used to detect the cytotoxicity of nanoparticles; finally using 3.0T magnetic resonance MRI system observation in vivo magnetic resonance imaging effect of nanoparticles. The prepared silica nanomaterials Gd-MSN gadopentetic acid doped TEM, Gd-MSN spherical morphology observation, Malvin measured the average particle size of about 105-128nm; ICP-AES doped gadolinium content measured up to 771.08 Mo L/g, Gd-MSN has a good stability in vitro environment, and there is no obvious cytotoxicity in the concentration of 25,50100 g/m L; in vitro and in vivo MRI results show that Gd-MSN can significantly reduce the T1 and T2 relaxation time for signal characteristics of short T1 and short T2. Conclusion the successful preparation of monodisperse, easy modification, new gadolinium doped nano material high loading, is expected to become a new target to multi functional magnetic resonance nano contrast agent.

【學(xué)位授予單位】：重慶醫(yī)科大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：R445.2

【參考文獻(xiàn)】

相關(guān)期刊論文 前8條

1 李曉溪;陳祿;楊美燕;;介孔二氧化硅納米粒子在載藥系統(tǒng)中的應(yīng)用研究進(jìn)展[J];中國新藥雜志;2015年13期

2 李金霞;;基于納米技術(shù)的癌癥早期診斷平臺(英文)[J];Science Bulletin;2015年04期

3 賀曠馳;王蒙;趙斌;何丹農(nóng);;介孔二氧化硅納米復(fù)合材料的研究進(jìn)展[J];材料導(dǎo)報;2014年13期

4 劉濤;孫麗寧;劉政;仇衍楠;施利毅;;稀土上轉(zhuǎn)換發(fā)光納米材料的應(yīng)用[J];化學(xué)進(jìn)展;2012年Z1期

5 趙曉琴;林敬東;廖代偉;張鴻斌;;單分散納米二氧化硅的制備及影響因素分析[J];廈門大學(xué)學(xué)報(自然科學(xué)版);2011年S1期

6 范艷玲;劉藝芳;呂雪莉;孟凡成;時孟琪;張香蘭;;硅酸乙酯為原料反相微乳液法制備納米二氧化硅[J];化學(xué)工業(yè)與工程;2010年05期

7 何曉曉;石碧華;王柯敏;陳冕;譚蔚泓;;基于反相微乳液法的尺寸可控性二氧化硅基于反相微乳液法的尺寸可控性二氧化硅納米顆粒制備研究[J];湖南大學(xué)學(xué)報(自然科學(xué)版);2010年04期

8 李東平;;納米二氧化硅的制備與表征[J];化學(xué)工程師;2007年08期

，

本文編號：1414527