本文選題：氧化鈀　切入點：電位型傳感器　出處：《物理化學(xué)學(xué)報》2017年03期

【摘要】：研究了基于氧化鈀(PdO)電極的電位型傳感器的敏感特性,并探討了其敏感機理。首先,利用Mg、Ni和La元素對PdO電極進行摻雜,將摻雜后的PdO電極印刷在氧化鋯電解質(zhì)上,制備成電位型傳感器,并對一氧化碳(CO)的敏感特性進行了測試。由于摻雜后的PdO電極表面缺陷增加,這有利于對CO的吸附,有效地提高了傳感器的靈敏度。其次,為了探究敏感信號的來源,PdO電極分別印刷在氧化鋁和沸石基片上,同樣測試了對CO的敏感特性。其中PdO電極與沸石所組成的電位型傳感器對CO濃度可以產(chǎn)生階梯型響應(yīng)。最后,對傳感器分別進行了電阻和阻抗譜的測量,測量結(jié)果表明:傳感器的響應(yīng)可以歸因于電極和電解質(zhì)之間界面電位的變化。綜合上述研究結(jié)果,建立了電偶層模型來解釋基于PdO電極的電位型傳感器的工作機理。
[Abstract]:The sensitivity characteristics and mechanism of potentiometric sensor based on PdO electrode were studied.Firstly, the PdO electrode was doped with Ni and La elements. The doped PdO electrode was printed on zirconia electrolyte to form a potentiometric sensor. The sensitive properties of CO were tested.Due to the increase of the surface defects of the doped PdO electrode, it is advantageous to the adsorption of CO, and the sensitivity of the sensor is improved effectively.The potential sensor composed of PdO electrode and zeolite can produce step response to CO concentration.Based on the above results, an electric couple layer model is established to explain the working mechanism of the potentiometric sensor based on PdO electrode.
【作者單位】： 寧波大學(xué)信息科學(xué)與工程學(xué)院;大連民族大學(xué)機電工程學(xué)院;
【基金】：supported by the National Natural Science Foundation of China(61471210,61501271,51472126) Natural Science Foundation of Ningbo Municipality,China(2015A610108) K.C.Wong Magna Fund in Ningbo University,China~~
【分類號】：TP212

【相似文獻】

相關(guān)會議論文 前1條

1 陳敏;范利萍;施春苗;鄭小明;;高性能Ce-Mn-O納米粉體的合成及涂層效應(yīng)研究[A];第十三屆全國催化學(xué)術(shù)會議論文集[C];2006年

相關(guān)重要報紙文章 前1條

1 記者 畢玉才　特約記者 劉勇;新型材料利用太陽光殺菌凈水[N];光明日報;2010年

相關(guān)博士學(xué)位論文 前1條

1 張?zhí)┎?若干流動體系中的化學(xué)反應(yīng)研究[D];中國科學(xué)技術(shù)大學(xué);2010年

相關(guān)碩士學(xué)位論文 前1條

1 喬俏;氧化鈀基敏感材料的制備及室溫氣敏特性研究[D];大連理工大學(xué);2016年

，

本文編號：1701957