【摘要】：制備了多孔摻鉺鈮酸鋰材料,并研究了其3波長(zhǎng)可見(jiàn)上轉(zhuǎn)換熒光特性.在980 nm連續(xù)光激發(fā)下發(fā)射峰中心波長(zhǎng)分別為660、550和450 nm.通過(guò)相干背散射法測(cè)得多孔鈮酸鋰的傳輸平均自由程在亞微米范圍,這使得制備的多孔摻鉺鈮酸鋰適用于可見(jiàn)光多波長(zhǎng)上轉(zhuǎn)換隨機(jī)激光.
[Abstract]:Porous erbium-doped lithium niobate materials were prepared and their three wavelength visible up-conversion fluorescence characteristics were studied. The central wavelengths of the emission peak are 660550 nm and 450nm respectively under the excitation of 980nm continuous light. The average free path of porous lithium niobate was measured by coherent backscattering method in the sub-micron range, which makes the porous erbium-doped lithium niobate suitable for multi-wavelength up-conversion random laser.
【作者單位】： 南開(kāi)大學(xué)泰達(dá)應(yīng)用物理研究院弱光非線(xiàn)性光子學(xué)教育部重點(diǎn)實(shí)驗(yàn)室;北京無(wú)線(xiàn)電計(jì)量測(cè)試研究所計(jì)量與校準(zhǔn)技術(shù)重點(diǎn)實(shí)驗(yàn)室;切爾諾維茨國(guó)立大學(xué)相關(guān)光學(xué)實(shí)驗(yàn)室;
【基金】：Supported by National Natural Science Foundation of China(11174161,10874093) National Basic Research Program of China(2010CB934101,2010CB93801) The 111 Project(B07013) Tianjin International Cooperation Program and Oversea Excellent Teacher Project(MS2010NKDX023)
【分類(lèi)號(hào)】：O482.31

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 劉名揚(yáng);王秀庭;;上轉(zhuǎn)換熒光強(qiáng)度與激光功率的關(guān)系[J];裝甲兵工程學(xué)院學(xué)報(bào);2011年03期

2 孟超,孟廣政,宋增福;上轉(zhuǎn)換發(fā)光的有效增強(qiáng)機(jī)制——上轉(zhuǎn)換敏化[J];光譜學(xué)與光譜分析;2001年02期

3 徐東勇,臧競(jìng)存;上轉(zhuǎn)換激光和上轉(zhuǎn)換發(fā)光材料的研究進(jìn)展[J];人工晶體學(xué)報(bào);2001年02期

4 佟建波;黃茜;張曉丹;張存善;趙穎;;納米Ag顆粒表面等離子激元對(duì)上轉(zhuǎn)換材料光致發(fā)光性能影響的研究[J];物理學(xué)報(bào);2012年04期

5 張合義,嚴(yán)懋勛;高靈敏度的上轉(zhuǎn)換熒光[J];光譜學(xué)與光譜分析;1985年06期

6 段玉生;;微球諧振腔光上轉(zhuǎn)換的研究[J];人工晶體學(xué)報(bào);2008年02期

7 李小燕;鄭志強(qiáng);馮卓宏;劉t，

本文編號(hào)：2016468