本文選題：電潤濕顯示器　切入點：疏水層性能恢復　出處：《華南師范大學學報(自然科學版)》2015年06期 　論文類型：期刊論文

【摘要】：以通過蒸汽溶解法(Vapor redissolve method)代替高溫回流法來恢復氟樹脂層的疏水性能,使用氟碳溶劑(HFE7100)蒸汽溶解氟樹脂層粗糙表面使其形成溶膠狀態(tài),加熱蒸發(fā)溶劑后使表面恢復疏水性質(zhì).對溶解法溶解時間、干燥溫度和干燥時間等條件進行了探究,對比了高溫回流法和蒸汽溶解法對電潤濕顯示器產(chǎn)生的物理和光電的影響.蒸汽溶解法在不影響電潤濕顯示器其他功能的前提下,可以替代高溫回流方法恢復氟樹脂層的疏水功能并且工藝更簡單.
[Abstract]:The hydrophobicity of fluorine resin layer was restored by using Vapor redissolve method instead of high temperature reflux method. The fluorocarbon solvent HFE7100) was used to dissolve the rough surface of fluorine resin layer to form a sol state. The hydrophobic property of the surface was restored after the evaporation solvent was heated. The conditions such as dissolution time, drying temperature and drying time were investigated. The physical and photoelectric effects of high temperature reflux method and steam dissolution method on the electrical wetting display are compared. The steam dissolution method does not affect the other functions of the electrical wetting display. It can replace the high temperature reflux method to restore the hydrophobic function of fluorine resin layer and the process is simpler.
【作者單位】： 華南師范大學華南先進光電子研究院;深圳國華光電科技有限公司;
【基金】：國家自然科學基金項目(21303060) 廣東省自然科學基金項目(S2013010014418) 教育部引進創(chuàng)新科研團隊項目(IRT13064) 廣東省創(chuàng)新科研團隊項目(2011D039)
【分類號】：TN873;TM21

【參考文獻】

相關(guān)期刊論文 前1條

1 李顯歌;白鵬飛;Rob Hayes;水玲玲;吳昊;竇盈瑩;郭媛媛;周國富;;Teflon AF1600作為電潤濕顯示器件疏水絕緣層的可靠性研究[J];華南師范大學學報(自然科學版);2015年02期

【共引文獻】

相關(guān)期刊論文 前1條

1 李坦;白鵬飛;林立新;李顯歌;蔣洪偉;周國富;;電潤濕顯示器件的電場動態(tài)響應(yīng)特性對其性能的影響[J];華南師范大學學報(自然科學版);2015年03期

，

本文編號：1575930