本文選題：混凝土裂縫　切入點：紅外熱成像法　出處：《重慶交通大學》2017年碩士論文

【摘要】：混凝土材料具有強度高、造價低廉、施工方便及就地取材等優(yōu)點被廣泛運用于水利工程建設(shè)中。然而在水泥水化熱、外荷載以及自然災害等因素的影響下,混凝土表面及內(nèi)部極易產(chǎn)生裂縫。尤其對于水工混凝土,裂縫的產(chǎn)生將在不同程度上影響結(jié)構(gòu)的整體性及耐久性,嚴重時還會影響到結(jié)構(gòu)的承載能力,引起工程事故。因此,尋找一種有效的無損檢測方法檢測混凝土中裂縫的位置及尺寸,對水利工程質(zhì)量評估提供參考具有重要意義�；诖�,本文采用紅外熱像法對混凝土內(nèi)部裂縫進行檢測,主要開展了以下研究工作:(1)介紹混凝土無損檢測方法、紅外熱成像無損檢測技術(shù)的應用與研究現(xiàn)狀。在現(xiàn)有的混凝土裂縫無損檢測方法的基礎(chǔ)上,將紅外熱像法引用出來,并應用到混凝土裂縫檢測當中,然后闡述紅外熱成像無損檢測相關(guān)理論、感應加熱理論。(2)采用基于輻射熱源的紅外熱像法檢測混凝土內(nèi)部裂縫。選用遠紅外石英加熱板和太陽輻射作為熱源對混凝土試件表面進行熱激勵,通過紅外熱像儀采集試件受熱激勵表面的溫度數(shù)據(jù),得到試件表面的溫度分布情況以及表面溫度隨時間的變化情況,通過對此結(jié)果進行分析來定位裂縫的位置、判斷裂縫的大小。(3)采用基于鋼筋感應加熱的紅外熱像法檢測混凝土內(nèi)部裂縫。選用高頻感應加熱儀對混凝土試件內(nèi)部鋼筋進行加熱,通過紅外熱像儀采集與感應加熱儀正對的試件表面的溫度數(shù)據(jù),得到試件表面的溫度分布情況以及表面溫度隨時間的變化情況,通過對此結(jié)果進行分析來定位裂縫的位置、判斷裂縫的大小。
[Abstract]:Concrete material has the advantages of high strength, low cost, convenient construction and local material selection. However, under the influence of hydration heat of cement, external load and natural disaster, etc. It is easy to produce cracks on the surface and inside of concrete. Especially for hydraulic concrete, the occurrence of cracks will affect the integrity and durability of the structure to some extent, and will also affect the bearing capacity of the structure when serious, and cause engineering accidents. It is of great significance to find an effective nondestructive testing method to detect the position and size of cracks in concrete, which can provide a reference for water conservancy engineering quality evaluation. Based on this, the infrared thermal image method is used to detect the internal cracks of concrete. The following research work is mainly carried out: (1) introducing the methods of nondestructive testing of concrete, the application and research status of infrared thermal imaging nondestructive testing technology. Based on the existing methods of nondestructive testing of concrete cracks, the infrared thermal image method is quoted. And applied to concrete crack detection, and then elaborated the infrared thermal imaging nondestructive testing related theory, The infrared thermal image method based on radiative heat source is used to detect the internal cracks of concrete. The far infrared quartz heating plate and solar radiation are used as heat sources to heat the surface of concrete specimen. The temperature data of the heated excited surface of the specimen were collected by infrared thermal imager, and the temperature distribution on the surface of the specimen and the change of the surface temperature with time were obtained. The location of the crack was located by analyzing the results. To determine the size of the crack, the infrared thermal image method based on induction heating of steel bar is used to detect the inner crack of concrete. The high frequency induction heating instrument is used to heat the steel bar inside the concrete specimen. The temperature distribution of the specimen surface and the change of the surface temperature with time are obtained by collecting the temperature data on the surface of the specimen which is directly aligned with the induction heating instrument by the infrared thermal imager. The location of the crack is located by analyzing the results. Judge the size of the crack.
【學位授予單位】：重慶交通大學
【學位級別】：碩士
【學位授予年份】：2017
【分類號】：TN219;TV544

【參考文獻】

相關(guān)期刊論文 前10條

1 楊智;張今陽;孔楠楠;;沖擊回波法檢測混凝土內(nèi)部缺陷[J];中國建材科技;2013年04期

2 趙珂;熊艷;趙敏;;基于近紅外光譜技術(shù)的臍橙快速無損檢測[J];激光與紅外;2011年06期

3 趙石彬;張存林;伍耐明;段玉霞;李艷紅;;紅外熱波無損檢測技術(shù)用于聚丙烯管道缺陷的檢測[J];光學學報;2010年02期

4 劉俊巖;戴景民;王揚;;紅外鎖相法熱波檢測技術(shù)及缺陷深度測量[J];光學精密工程;2010年01期

5 李艷紅;趙躍進;張存林;;半透明材料涂層的紅外檢測[J];光學精密工程;2009年07期

6 霍雁;趙躍進;李艷紅;張存林;;脈沖和鎖相紅外熱成像檢測技術(shù)的對比性研究[J];激光與紅外;2009年06期

7 李艷紅;趙躍進;馮立春;張存林;武頌;朱軍輝;;碳纖維基體涂層質(zhì)量的紅外熱波檢測研究[J];中國激光;2009年06期

8 陳祥森;;混凝土缺陷無損檢測技術(shù)發(fā)展現(xiàn)狀綜述[J];福建建材;2007年01期

9 劉建武;;混凝土裂縫產(chǎn)生的成因與控制措施[J];水運工程;2006年01期

10 張淑儀;超聲紅外熱像技術(shù)及其在無損評價中的應用[J];應用聲學;2004年05期

相關(guān)博士學位論文 前3條

1 趙延廣;基于鎖相紅外熱像理論的無損檢測及疲勞性能研究[D];大連理工大學;2012年

2 劉慧;超聲紅外鎖相熱像無損檢測技術(shù)的研究[D];哈爾濱工業(yè)大學;2010年

3 汪子君;紅外相位法無損檢測技術(shù)及應用研究[D];哈爾濱工業(yè)大學;2010年

相關(guān)碩士學位論文 前2條

1 樊丹丹;基于紅外熱波的界面脫粘無損檢測技術(shù)研究[D];中北大學;2011年

2 魏敦軍;軍用飛機紅外熱波無損檢測技術(shù)研究[D];武漢理工大學;2007年

，

本文編號：1668109