【摘要】：采用電化學(xué)阻抗、絲束電極、SEM/EDS和XRD的分析方法,研究原油沉積水對Q235B碳鋼腐蝕行為的影響。結(jié)果表明,碳鋼在沉積水中浸泡21 d過程中,腐蝕速率逐漸降低,腐蝕形式以均勻腐蝕為主;而從21~35 d浸泡過程中,碳鋼的腐蝕速率逐漸增大,且腐蝕程度加劇,腐蝕形態(tài)由均勻腐蝕為主轉(zhuǎn)變?yōu)橐渣c(diǎn)蝕為主的局部腐蝕,點(diǎn)蝕的大小和密集度增加。這是由于在起始階段,碳鋼表面沉積一層CaCO_3,有效地阻礙了腐蝕,而隨著時間的延長,CaCO_3逐漸失去對碳鋼基體的保護(hù),從而加速局部腐蝕的發(fā)生。
[Abstract]:The effect of crude oil deposition water on corrosion behavior of Q235B carbon steel was studied by electrochemical impedance, wire beam electrode, SEM/EDS and XRD. The results show that the corrosion rate of carbon steel decreases gradually during 21 days immersion in the deposited water, and the corrosion form is mainly uniform corrosion. The corrosion rate and corrosion degree of carbon steel increased gradually from 21 to 35 days, and the corrosion morphology changed from uniform corrosion to pitting local corrosion, and the size and intensity of pitting corrosion increased. This is due to the fact that at the initial stage, a layer of CaCO_3, deposited on the surface of carbon steel effectively hinders corrosion, but with the extension of time, CaCO_3 gradually loses the protection of the carbon steel substrate, thus accelerating the occurrence of local corrosion.
【作者單位】： 中國石化青島安全工程研究院;中國石化石油化工科學(xué)研究院;中國科學(xué)院寧波材料技術(shù)與工程研究所;
【基金】：中國石化安全工程研究院資金(Y-199和Y-200) 國家自然科學(xué)基金(41506098) 中國博士后基金和第九批特等(2015M580528和2016T90553) 寧波市自然科學(xué)基金(2016A610261)~~
【分類號】：TE988

【相似文獻(xiàn)】

相關(guān)期刊論文 前5條

1 鄔康迪;曾為民;汪文強(qiáng);馬玉錄;;原油儲罐沉積水腐蝕的靜態(tài)掛片實(shí)驗研究[J];化工裝備技術(shù);2013年06期

2 汪文強(qiáng);曾為民;馬玉錄;;碳鋼在原油儲罐沉積水中的電化學(xué)行為[J];腐蝕與防護(hù);2014年04期

3 賈思洋;李超;韓東銳;;B610E不同焊接接頭在石油沉積水中的耐蝕性研究[J];裝備環(huán)境工程;2012年06期

4 李超;賈思洋;張波;;儲罐鋼08MnNiVR和SPV490Q在石油沉積水中腐蝕性能對比[J];裝備環(huán)境工程;2013年05期

5 ;[J];;年期

，

本文編號：2423478