本文選題：不銹鋼　切入點(diǎn)：臨界點(diǎn)蝕溫度　出處：《腐蝕與防護(hù)》2017年06期 　論文類型：期刊論文

【摘要】：在外加恒電位下,通過測腐蝕電流密度-溫度曲線的方法研究了Cl~-含量對316L不銹鋼臨界點(diǎn)蝕溫度(CPT)的影響。結(jié)果表明:在臨界點(diǎn)蝕溫度以下,試樣表面鈍化膜比較穩(wěn)定,超過該溫度后,試樣表面開始發(fā)生點(diǎn)蝕。Cl~-含量越高,316L不銹鋼臨界點(diǎn)蝕溫度越低,且表面的點(diǎn)蝕坑越多�，F(xiàn)場的腐蝕產(chǎn)物分析表明,腐蝕產(chǎn)物表面稀疏,主要元素為O、Fe、C、Cl。現(xiàn)場生產(chǎn)水Cl~-質(zhì)量濃度高達(dá)21.431g/L,對316L不銹鋼的腐蝕極其嚴(yán)重。
[Abstract]:The effect of Cl-content on the critical pitting temperature (CPT) of 316L stainless steel was studied by measuring the corrosion current density-temperature curve under constant potential. The results show that the passivation film on the surface of 316L stainless steel is stable under the critical pitting temperature. When the temperature exceeds this temperature, the surface of the sample begins to undergo pitting. The higher the content of Cl--is, the lower the critical pitting temperature of stainless steel is, and the more pitting pits are on the surface. The analysis of corrosion products in the field shows that the surface of corrosion products is sparse. The main element is OFE CnCl. The concentration of Cl-mass in water is 21.431 g / L and the corrosion of 316L stainless steel is very serious.
【作者單位】： 西南石油大學(xué)石油與天然氣工程學(xué)院;
【分類號】：TE983;TG172.9

【相似文獻(xiàn)】

相關(guān)期刊論文 前5條

1 雷冰;馬元泰;李瑛;王福會;常澤亮;謝俊峰;宋文文;周理志;;模擬高溫高壓氣井環(huán)境中HP2-13Cr的點(diǎn)蝕行為研究[J];腐蝕科學(xué)與防護(hù)技術(shù);2013年02期

2 王獻(xiàn)f ;含鉻油套管鋼的CO_2腐蝕點(diǎn)蝕特征研究[J];全面腐蝕控制;2002年06期

3 孫冬柏,李靜,俞宏英,路民旭,嚴(yán)密林,趙國仙;Ca~(2+)和Mg~(2+)對CO_2環(huán)境中點(diǎn)蝕形貌的影響[J];鋼鐵研究學(xué)報;2001年03期

4 張國超;林冠發(fā);張涓濤;;超級13Cr油套管鋼的點(diǎn)蝕行為研究[J];焊管;2013年07期

5 ;[J];;年期

相關(guān)碩士學(xué)位論文 前2條

1 王軍;原油儲罐底板內(nèi)腐蝕環(huán)境中的點(diǎn)蝕行為研究[D];中國石油大學(xué)(華東);2014年

2 曹治栓;油罐底板點(diǎn)蝕深度的數(shù)值模擬預(yù)測研究[D];中國石油大學(xué)（華東）;2013年

，

本文編號：1600856