【摘要】：通過實驗方法分析汽車板涂裝后漆膜產(chǎn)生點蝕的原因。利用S-3400N掃描電子顯微鏡(SEM)觀察腐蝕產(chǎn)物微觀形貌,輔以能譜(EDS)分析點蝕部位元素分布和含量。結(jié)果表明,冷軋汽車板表面夾雜物降低了其表面磷化膜的覆蓋性、均勻性,易使涂裝后的漆膜發(fā)生點蝕。通過控制鑄坯機清深度可有效改善冷軋板表面狀態(tài),降低基板表面夾雜物數(shù)量。
[Abstract]:The causes of pitting corrosion of paint film after painting of automobile board are analyzed by experimental method. The micromorphology of corrosion products was observed by S 鈮，

本文編號：2481557