本文選題：砂巖 + PVD涂層刀具　； 參考：《機(jī)械設(shè)計與制造》2017年12期

【摘要】：砂巖裝飾品已逐漸走進(jìn)人們的生活,提高砂巖加工表面質(zhì)量已備受關(guān)注。利用正交試驗,研究PVD涂層刀具高速銑削砂巖的切削速度、進(jìn)給速度及切削深度對加工表面粗糙度的影響。分析了表面粗糙度隨不同切削參數(shù)的變化規(guī)律:隨著進(jìn)給速度與切削深度的增加,表面粗糙度值變大,隨著切削速度的增加,表面粗糙度值減小,當(dāng)切削速度由3000r/min提高到12000r/min時,表面粗糙度值由4.98μm減小到3.64μm。建立了表面粗糙度的回歸預(yù)測模型,經(jīng)F檢驗具有較高的顯著性,為實際生產(chǎn)加工砂巖制品提供了一定理論依據(jù)與參考價值。
[Abstract]:Sandstone ornaments have gradually come into people's lives, and the improvement of sandstone surface quality has attracted much attention. The effects of cutting speed, feed speed and cutting depth on the surface roughness of high speed milling sandstone with PVD coated tool were studied by orthogonal test. The variation of surface roughness with different cutting parameters is analyzed. With the increase of feed speed and cutting depth, the surface roughness value becomes larger, and with the increase of cutting speed, the surface roughness value decreases. When the cutting speed is increased from 3000r/min to 12000r/min, The surface roughness decreased from 4.98 渭 m to 3.64 渭 m. The regression prediction model of surface roughness is established. The F test has a high significance and provides a certain theoretical basis and reference value for the actual production and processing of sandstone products.
【作者單位】： 包頭鋼鐵職業(yè)技術(shù)學(xué)院;
【分類號】：TD985

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 ;高速銑削器[J];探礦工程;1980年02期

2 何柏林，邵爾玉，于影霞;表面粗糙度和硬度的匹配性對接觸疲勞性能的影響[J];熱加工工藝;1995年03期

3 賈紅艷;鍍覆零件表面粗糙度的標(biāo)注方法[J];煤炭科技;2003年04期

4 谷春仙;;涂層刀具的應(yīng)用[J];陜西煤炭技術(shù);1989年01期

相關(guān)博士學(xué)位論文 前1條

1 曹麗麗;煤系砂巖滲流—蠕變損傷破裂機(jī)理及其分?jǐn)?shù)階模型研究[D];中國礦業(yè)大學(xué);2017年

，

本文編號：2091831