本文選題：銅冶煉 + 爐渣浮選尾礦　； 參考：《金屬礦山》2017年12期

【摘要】：尾礦的大量囤積已成為制約冶煉過程可持續(xù)發(fā)展的重要因素,從尾礦中回收有價金屬元素可以降低企業(yè)資源的過度浪費,減少對周邊環(huán)境的污染,同時提高資源的綜合回收率。對某銅冶煉爐渣浮選尾礦采用硫酸浸出工藝進行試驗,考察了初始pH、液固比、浸出時間和浸出溫度對銅浸出率的影響。結(jié)果表明:在初始pH=3、浸出時間為12 h、液固比為4 m L/g、浸出溫度為90℃條件下,銅的浸出率達到78.53%,H2SO4用量為23.57 kg/t,其余雜質(zhì)元素浸出率較低。對銅浸出過程動力學(xué)模型研究表明,該硫酸浸出過程符號內(nèi)擴散模型,反應(yīng)的表觀活化能為23.961k J/mol。
[Abstract]:The heavy hoarding of tailings has become an important factor restricting the sustainable development of smelting process. The recovery of valuable metal elements from tailings can reduce the excessive waste of the enterprise resources, reduce the pollution to the surrounding environment, and improve the comprehensive recovery rate of the resources. The effect of initial pH, liquid-solid ratio, leaching time and leaching temperature on copper leaching rate, the results show that the leaching rate of copper is 78.53%, H2SO4 dosage is 23.57 kg/t, and the leaching rate of other impurities is low. The kinetics model of copper leaching process is studied at initial pH=3, the leaching time is 12 h, the liquid to solid ratio is 4 m L/g and the leaching temperature is 90. It shows that the apparent activation energy of the reaction is 23.961k J/mol. in the sulfuric acid leaching process.
【作者單位】： 江西理工大學(xué)冶金與化學(xué)工程學(xué)院;
【基金】：國家自然科學(xué)基金項目(編號:51564021) 江西省自然科學(xué)基金項目(編號:20151BAB206028) 江西省重點研發(fā)計劃項目(編號:20171BBG70041)
【分類號】：TD923;TD926.4

【相似文獻】

相關(guān)期刊論文 前8條

1 陳焱;路南;;鍺鎵礦石的硫酸浸出[J];世界采礦快報;1992年11期

2 張文鉦;;硝酸硫酸浸出鉬精礦現(xiàn)狀和進展[J];鉬業(yè)經(jīng)濟技術(shù);1989年03期

3 張澤強,沈上越;光催化氧化預(yù)處理對硫酸浸出硫化銅精礦的影響[J];有色金屬(選礦部分);2004年05期

4 鄭占千;;淺析銅渣焙燒溫度與焙砂硫酸浸出的關(guān)系[J];新疆有色金屬;2010年S1期

5 文健;王琳;;錳結(jié)核礦的硫酸浸出[J];世界采礦快報;1990年02期

6 卡里諾;汪焰臺;劉尚勇;;加拿大格爾夫礦物公司拉比特湖鈾廠鈾的回收[J];鈾礦選冶;1980年06期

7 鄭永興;文書明;鄭海雷;鄧久帥;劉建;;含銅難處理鐵礦的硫酸浸出試驗研究[J];礦產(chǎn)綜合利用;2011年01期

8 李金生;李杰;雷麗;王亮娟;樊占國;;富硼渣制備硼酸及回收硫酸鎂的新研究[J];礦產(chǎn)綜合利用;2011年03期

相關(guān)碩士學(xué)位論文 前1條

1 李濤;改性鎢尾礦地聚合物的制備及其性能研究[D];江西理工大學(xué);2017年

，

本文編號：1980310