本文選題：膠凝材料 + 尾砂膠結充填體�。� 參考：《礦業(yè)研究與開發(fā)》2017年03期

【摘要】：針對膠固粉和硅酸鹽水泥對尾砂膠結充填體抗壓強度的影響進行了對比實驗研究,測得不同濃度、不同灰砂比和充填體在不同齡期下的抗壓強度。實驗結果顯示:在灰砂比和濃度相同條件下,隨齡期的增加,膠固粉膠結充填體強度增長明顯,28d齡期膠固粉充填體強度明顯高于水泥充填體強度值,60d齡期膠固粉充填體強度增加值依然顯著;低灰砂比膠固粉尾砂膠結充填不僅滿足礦山充填強度的要求,并降低了充填成本,具有良好的效益。
[Abstract]:The effects of cementing powder and Portland cement on the compressive strength of tailings cemented filling were studied. The experimental results show that under the condition of the same ratio of ash to sand and the same concentration, with the increase of age, The strength of cemented cement filling was significantly higher than that of cement filling at 28 days of age. The cemented filling of tailings with low lime-sand ratio not only meets the requirements of mine filling strength, but also reduces the filling cost and has good benefit.
【作者單位】： 華北理工大學礦業(yè)工程學院;河北省礦業(yè)開發(fā)與安全技術重點實驗室;河北鋼鐵集團礦業(yè)有限公司石人溝鐵礦;
【基金】：河北省自然科學基金項目(E2016209224);河北省自然科學基金項目(E2015209172)
【分類號】：TD853.343

【參考文獻】

相關期刊論文 前8條

1 姚中亮;;結構流體膠結充填技術應用及展望[J];礦業(yè)研究與開發(fā);2016年10期

2 董培鑫;王忠紅;高謙;袁國斌;;鞍鋼礦山全尾砂新型充填膠凝材料配方正交試驗與優(yōu)化[J];礦業(yè)研究與開發(fā);2015年12期

3 孫光華;魏莎莎;蘇東良;;基于正交試驗的全尾砂膠結充填配比方案優(yōu)化[J];金屬礦山;2015年04期

4 楊志強;高謙;王永前;倪文;陳得信;;利用金川水淬鎳渣尾砂開發(fā)新型充填膠凝劑試驗研究[J];巖土工程學報;2014年08期

5 董璐;高謙;南世卿;杜聚強;;超細全尾砂新型膠結充填料水化機理與性能[J];中南大學學報(自然科學版);2013年04期

6 孫慶巍#講師;朱涵;崔正龍;;粉煤灰-煤矸石基膠結充填材料制備與性能研究[J];中國安全科學學報;2012年11期

7 杜聚強;高謙;南世卿;董璐;;一種全尾砂充填新型膠凝材料的研制[J];金屬礦山;2012年05期

8 李一帆,張建明,鄧飛,白世偉;深部采空區(qū)尾砂膠結充填體強度特性試驗研究[J];巖土力學;2005年06期

【共引文獻】

相關期刊論文 前10條

1 劉音;劉洋;周煜明;路瑤;崔博強;郭皓;;機械研磨時間對粗粉煤灰基充填膠凝材料性能的影響[J];煤炭科學技術;2017年06期

2 侯永強;張耀平;王磊;;不同尾砂充填體強度及沉降性能對比分析[J];煤炭技術;2017年06期

3 楊志強;王永前;高謙;王虎;;金川鎳礦廢棄物在充填采礦中利用現(xiàn)狀與展望[J];礦產(chǎn)綜合利用;2017年03期

4 魏曉明;李長洪;張立新;周小龍;羅文沖;;高階段嗣后膠結充填體配比參數(shù)設計及工程優(yōu)化[J];采礦與安全工程學報;2017年03期

5 宋衛(wèi)東;朱鵬瑞;戚偉;唐亞男;;三軸作用下巖柱-充填體試件耦合作用機理研究[J];采礦與安全工程學報;2017年03期

6 甘德清;韓亮;劉志義;趙海鑫;蔡曉盛;;尾砂粒級組成對充填體強度特性影響的試驗研究[J];化工礦物與加工;2017年04期

7 孫光華;葉洪濤;劉志義;龔君放;路燕澤;;膠固粉尾砂膠結充填體強度實驗研究[J];礦業(yè)研究與開發(fā);2017年03期

8 李小明;沈苗;王，

本文編號：1959205