本文選題：云母礦 + 浮選�。� 參考：《化工礦物與加工》2017年12期

【摘要】：某云母礦主要成分為云母和石英,云母品位達到34.58%,為綜合利用該資源,進行了選礦富集及精礦漂白試驗研究,應用所開發(fā)的浮選—加酸細磨工藝取得了較好的技術(shù)指標。浮選精礦云母品位達到98.95%,回收率為86.64%,白度為82.20%。浮選精礦經(jīng)加酸細磨漂白處理后,鐵質(zhì)量分數(shù)由0.83%降低至0.43%,TiO2質(zhì)量分數(shù)由0.47%降低至0.32%,白度提高到98.50%,d90為14.894μm,d50達到4.268μm。
[Abstract]:The main components of a mica ore are mica and quartz, and the grade of mica reaches 34.58. In order to make comprehensive use of this resource, the experiments of concentrate concentration and concentrate bleaching have been carried out, and a good technical index has been obtained by using the floatation-acid fine grinding process developed.The grade of mica in flotation concentrate is 98.95, the recovery is 86.64 and the whiteness is 82.20.After the flotation concentrate was bleached by adding acid, the mass fraction of iron decreased from 0.83% to 0.43%, the mass fraction of TiO2 decreased from 0.47% to 0.32%, and the whiteness of flotation concentrate increased to 98.50 渭 md90, 14.894 渭 md50 and 4.268 渭 m respectively.
【作者單位】： 長沙礦冶研究院有限責任公司;
【分類號】：TD97

【相似文獻】

相關(guān)期刊論文 前9條

1 高惠民,袁繼祖,譚超兵,雷蕓;安徽廬江絹云母磁選—漂白試驗研究[J];礦產(chǎn)保護與利用;2003年04期

2 雷蕓,袁繼祖,高惠民;安徽廬江絹云母磁選漂白試驗研究[J];武漢化工學院學報;2004年02期

3 謝修品,葉家興;郭山高嶺土高梯度磁分離與化學漂白試驗研究[J];非金屬礦;1986年01期

4 高惠民，張凌燕，，劉理根，袁楚雄;浙江伊利石絹云母礦物漂白試驗研究[J];化工礦山技術(shù);1996年01期

5 孫彥彬,王澤利,羅傳亮;吉林某地瓷石的酸浸除鐵漂白試驗[J];礦產(chǎn)綜合利用;2003年02期

6 于福家,韓躍新;磨機細磨介質(zhì)優(yōu)化研究[J];金屬礦山;1997年03期

7 肖慶飛;石貴明;段希祥;;新型細磨介質(zhì)的材質(zhì)選擇及應用研究[J];礦冶;2006年01期

8 凌永發(fā),段希祥;細磨介質(zhì)形狀的選擇及應用研究[J];有色金屬(選礦部分);2001年06期

9 吳彩斌,周慧芳,段希祥;鑄鐵段取代鋼球細磨的對比試驗研究[J];有色金屬(選礦部分);2004年06期

本文編號：1738947