Effect of Al22Si/ZL102 bimetal interface fabricated by extru
發(fā)布時(shí)間：2022-10-10 14:07
The Al22Si/ZL102 bimetal was designed and prepared by extrusion at near-eutectic temperature.The properties and fracture behaviors of different surface treatments between oxide film and zinc coating were compared between the Al22 Si and ZL102 bimetal.The average bonding strength of bimetal with intermittent oxide film interface was about 89.3MPa,which is higher than that of the bimetal fabricated by zinc coating method（about 76.3MPa）.During the process of extrusion,the oxidation film was extrude...
【文章頁(yè)數(shù)】：6 頁(yè)
【文章目錄】：
1. Introduction
2. Experimental
2.1. Experimental materials and process
2.2. Metallographic examination and mechanical testing
3. Results and Discussion
4. Conclusions
【參考文獻(xiàn)】：
碩士論文
[1]ZL201鑄造鋁合金副車架集成計(jì)算初步研究[D]. 陳俊宇.昆明理工大學(xué) 2020
本文編號(hào)：3689756
【文章頁(yè)數(shù)】：6 頁(yè)
【文章目錄】：
1. Introduction
2. Experimental
2.1. Experimental materials and process
2.2. Metallographic examination and mechanical testing
3. Results and Discussion
4. Conclusions
【參考文獻(xiàn)】：
碩士論文
[1]ZL201鑄造鋁合金副車架集成計(jì)算初步研究[D]. 陳俊宇.昆明理工大學(xué) 2020
本文編號(hào)：3689756
本文鏈接：http://sikaile.net/kejilunwen/jiagonggongyi/3689756.html
最近更新
教材專著