【摘要】：使用自主研制的MCJNi1K低碳中錳高硅焊絲對Q460E低合金高強鋼進行埋弧焊接試驗,對不同熱輸入條件下焊縫金屬的組織和性能進行了研究。結果表明,在一定的范圍內(nèi)隨熱輸入增大,焊縫金屬低溫沖擊韌性先增大再降低。當熱輸入為21.92 k J/cm時,低溫沖擊韌性最高,焊縫區(qū)隨組織主要為針狀鐵素體,斷口有韌窩特征。熱輸入較小或較大時,焊縫區(qū)分別有先共析鐵素體和魏氏組織產(chǎn)生,均會降低低溫沖擊韌性。
[Abstract]:The submerged arc welding test of Q460E low alloy high strength steel was carried out using MCJNi1K low carbon medium manganese high silicon welding wire. The microstructure and properties of weld metal under different thermal input conditions were studied. The results show that the low temperature impact toughness of weld metal increases first and then decreases with the increase of heat input in a certain range. When the heat input is 21.92k J/cm, the low temperature impact toughness is the highest, the weld zone is mainly acicular ferrite with microstructure, and the fracture has dimple characteristics. When the heat input is small or large, there are preeutectoid ferrite and Weiss microstructure in the weld zone, which can reduce the impact toughness at low temperature.
【作者單位】： 武漢理工大學材料科學與工程學院;
【分類號】：TG457.11

【相似文獻】

相關期刊論文 前10條

1 李廷忠;吳圣川;;等離子熔積成形熱輸入數(shù)學模型研究[J];電焊機;2006年06期

2 羅愛輝;張延松;陳關龍;朱文峰;;基于有限元法的電阻點焊電極熱輸入機理[J];焊接學報;2008年05期

3 及玉梅;付魁軍;徐光;翟曉莉;;船板生產(chǎn)工藝對高熱輸入焊接性能影響的對比與分析[J];焊接;2007年05期

4 俞海良;蘆鳳桂;蘇冬梅;裴培;姚舜;;熱輸入對焊縫金屬組織性能影響的預測及試驗研究[J];焊接技術;2008年02期

5 張德勤,田志凌,杜則裕,云紹輝;熱輸入對X65鋼焊縫金屬組織及性能的影響[J];焊接學報;2001年05期

6 夏佃秀;尚成嘉;孫衛(wèi)華;侯東華;陳曄;;低合金高強鋼大熱輸入焊接熱影響區(qū)組織性能[J];焊接學報;2011年04期

7 婁宇航;肖紅軍;田志凌;彭增華;;熱輸入對E40鋼雙絲埋弧焊焊縫組織及性能的影響[J];材料科學與工藝;2013年01期

8 丁福保,馬玉江,陳一清;不同熱輸入的低合金鋼HAZ中組織、夾雜對韌性的影響[J];焊接學報;1984年04期

9 于華,張柯柯,陳天杰,崔慧君;熱輸入對A517、A537鋼沖擊性能的影響[J];熱加工工藝;2005年05期

10 張婷婷;王文先;閆志峰;王志斌;張心保;;熱輸入對445J2超純鐵素體不銹鋼焊接接頭顯微組織和力學性能的影響[J];太原理工大學學報;2014年02期

相關重要報紙文章 前1條

1 ;大熱輸入焊接用中厚板生產(chǎn)技術[N];世界金屬導報;2012年

相關博士學位論文 前3條

1 石明浩;微鋯鋼大熱輸入焊接熱影響區(qū)性能及組織演變規(guī)律的研究[D];東北大學;2014年

2 張朋彥;大熱輸入焊接用鋼的制造工藝及其產(chǎn)業(yè)化技術研究[D];東北大學;2011年

3 阿榮;大熱輸入鋼焊縫組織及韌性改善[D];鋼鐵研究總院;2014年

相關碩士學位論文 前1條

1 婁宇航;E40鋼大熱輸入焊接接頭組織與性能研究[D];昆明理工大學;2012年

，

本文編號：2225267