【摘要】：采用井式坩堝爐熔煉鑄造了3種鋁合金,通過金相分析、硬度測試、力學(xué)拉伸、斷口掃描研究了過渡族元素對7136鋁合金組織和性能的影響。結(jié)果表明,過渡族元素能夠細(xì)化鑄態(tài)組織,復(fù)合添加Cr、Mn、Ti后晶粒細(xì)化效果明顯,能夠抑制鋁合金板材再結(jié)晶,提高抗拉強度,使伸長率提高15%,改變了斷裂方式,提高了綜合力學(xué)性能。
[Abstract]:Three kinds of aluminum alloys were cast in a well crucible furnace. The effect of transition elements on the microstructure and properties of 7136 aluminum alloy was studied by metallographic analysis, hardness test, mechanical tensile test and fracture scanning. The results show that the transition elements can refine the as-cast structure, and the effect of grain refinement is obvious after the addition of Cr,Mn,Ti, which can inhibit the recrystallization of aluminum alloy plate, improve the tensile strength, increase the elongation by 15%, and change the fracture mode. The comprehensive mechanical properties are improved.
【作者單位】： 煙臺南山學(xué)院工學(xué)院材料系;中南大學(xué)材料科學(xué)與工程學(xué)院;
【分類號】：TG146.21

【相似文獻(xiàn)】

相關(guān)期刊論文 前7條

1 劉玉梅,李吉學(xué),劉宏建,蘇文輝;少量元素?fù)诫s對Y-Ba-Cu-O強化的影響[J];吉林大學(xué)自然科學(xué)學(xué)報;1989年01期

2 楊恩波;;離子交換色譜法分離鈾同位素[J];中國原子能科學(xué)研究院年報;1986年00期

3 李東;劉羽寅;;鈦合金熱穩(wěn)定性研究 Ⅱ.過渡族元素在Ti_3X相形成中的行為[J];金屬學(xué)報;1984年06期

4 王永海;梁忠華;毛翔;;7022-T6、T73和T76熱處理狀態(tài)的電鏡觀察[J];輕合金加工技術(shù);1993年06期

5 崔玉友,李東,萬曉景;Ti合金中ω相的形成規(guī)律[J];金屬學(xué)報;1993年02期

6 張彥生;γ-Fe-Mn-Al-Cr-Si系合金Néel溫度與合金成分的關(guān)系[J];材料科學(xué)進(jìn)展;1988年02期

7 ;[J];;年期

相關(guān)會議論文 前1條

1 朱祥坤;郭躍玲;何學(xué)賢;楊淳;張巧大;;過渡族元素同位素分異理論體系及其在全球環(huán)境變化研究中的應(yīng)用[A];“十五”重要地質(zhì)科技成果暨重大找礦成果交流會材料四——“十五”地質(zhì)行業(yè)重要地質(zhì)科技成果資料匯編[C];2006年

相關(guān)碩士學(xué)位論文 前1條

1 張宇;過渡族元素添加對CuZr基金屬玻璃耐蝕性的影響[D];東北大學(xué);2011年

，

本文編號：2220426