【摘要】：研究了2397-T87鋁鋰合金的高周疲勞性能及裂紋萌生擴(kuò)展行為。結(jié)果表明:在應(yīng)力比R=0.1時(shí),2397-T87鋁鋰合金L方向、LT方向和ST方向光滑試樣(K_t=1.0)的疲勞壽命極限分別約為192,243和151 MPa;缺口試樣(K_t=3.0)的疲勞壽命極限分別約為72,78和70 MPa。其疲勞裂紋主要萌生于試樣表面,以及氧化物、夾雜等脫落形成的空洞,Al(CuFeMn)第二相雜質(zhì)粒子。駐留滑移帶(PSB)和晶粒取向?qū)ζ淦诹鸭y早期擴(kuò)展有重要影響。
[Abstract]:The high cycle fatigue properties and crack initiation propagation behavior of 2397-T87 Al-Li alloy were studied. The results show that the fatigue life limits of the L direction and St direction smooth specimens of Al-Li alloy R = 0.1 are about 192243 MPa and 151MPa, respectively, and the fatigue life limits of notched specimens (KTN 3.0) are about 72 78 and 70 MPA, respectively. The fatigue crack mainly originates on the surface of the specimen, and the second phase impurity particles of Al (CuFeMn) formed by the exfoliation of oxide and inclusions. The presence slip band (PSB) and grain orientation have important effects on the early growth of fatigue crack.
【作者單位】： 中南大學(xué)有色金屬材料科學(xué)與工程教育部重點(diǎn)實(shí)驗(yàn)室;
【基金】：國(guó)家重點(diǎn)基礎(chǔ)研究發(fā)展規(guī)劃(“973”計(jì)劃)(2012CB619503)
【分類號(hào)】：TG146.21

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 韓光煒，宋余九;慢加載條件下氫對(duì)裂紋萌生與擴(kuò)展的作用[J];金屬學(xué)報(bào);1994年10期

2 梅冰,李友國(guó),汪長(zhǎng)安,竇鵬;中碳貝氏體鋼滾動(dòng)接觸疲勞的裂紋萌生[J];清華大學(xué)學(xué)報(bào)(自然科學(xué)版);2002年12期

3 段興旺;劉建生;鄭曉華;黑志剛;;316LN鋼裂紋萌生的臨界損傷值[J];塑性工程學(xué)報(bào);2013年03期

4 魯連濤;鹽澤和章;;高速工具鋼的超長(zhǎng)壽命S-N曲線特征和內(nèi)部裂紋萌生行為[J];機(jī)械工程學(xué)報(bào);2006年12期

5 宋虎;王愛琴;李繼文;;A356合金原位拉伸裂紋萌生與擴(kuò)展行為分析[J];熱加工工藝;2010年06期

6 朱曉鋒;陸永浩;楊海波;;相界面對(duì)核電Z3CN20-09M不銹鋼裂紋萌生和擴(kuò)展的影響[J];材料科學(xué)與工藝;2013年05期

7 鄭賢淑,李治,金俊澤;基于凝固進(jìn)程數(shù)值模擬的鑄件裂紋預(yù)測(cè)方法[J];材料研究學(xué)報(bào);2000年S1期

8 杜洪奎;潘家禎;;低合金鋼微缺陷的裂紋萌生擴(kuò)展規(guī)律[J];機(jī)械工程材料;2008年02期

9 張紀(jì)奎;酈正能;;鈦合金結(jié)構(gòu)疲勞全壽命計(jì)算方法研究[J];機(jī)械強(qiáng)度;2010年03期

10 鄢文彬,涂銘旌;結(jié)構(gòu)鋼在低溫下沖擊斷裂時(shí)的裂紋萌生與擴(kuò)展[J];西安交通大學(xué)學(xué)報(bào);1981年06期

相關(guān)碩士學(xué)位論文 前1條

1 張文;含埋藏球型缺陷管道蠕變裂紋萌生的預(yù)測(cè)[D];天津大學(xué);2015年

，

本文編號(hào)：2127735