文獻(xiàn)名稱：電磁場(chǎng)頻率對(duì)電磁鑄造4045合金微觀組織的影響

    前言：采用低頻電磁半連續(xù)鑄造技術(shù)制備40 45鋁合金鑄坯,比較了常規(guī)DC法與低頻電磁鑄造40 45鋁合金圓錠(直徑為10 0mm)微觀組織的形貌。重點(diǎn)考察在10～5 0Hz范圍內(nèi),不同的頻率使電磁鑄造40 45鋁合金圓錠微觀組織發(fā)生的變化。結(jié)果表明:電磁場(chǎng)頻率顯著影響合金凝固的微觀組織,當(dāng)頻率由5 0Hz降低到15Hz時(shí),微觀組織分布趨于均勻,初晶αAl晶粒尺寸減小,二次枝晶臂減少,共晶Si形貌由條狀變?yōu)辄c(diǎn)狀,組織得到明顯細(xì)化。
    The difference of microstructures of 4045 aluminum alloy ingots with 100 mm in diameter cast by DC and LFEC (low frequency electromagnetic casting) processes was compared.The effects of electromagnetic frequency,ranging in 10～50 Hz,on the microstructure of 4045 aluminum alloy castings were focused on.The results showed that electromagnetic frequency greatly affects the microstructure of as-cast ingot.Uniform microstructure can be obtained and primary α-Al grain size and secondary dendrite are reduced,and eu...

文獻(xiàn)名稱 電磁場(chǎng)頻率對(duì)電磁鑄造4045合金微觀組織的影響

Article Name
英文(英語(yǔ))翻譯 Effects of Frequency on Microstructure of 4045 Aluminum DC Casting under Electromagnetic Field;

作者 李業(yè)欣; 崔建忠; 秦克;

Author Li Yexin Cui Jianzhong Qin Ke （Northeastern University;Shenyang;China）;

作者單位
Author Agencies 東北大學(xué);

文獻(xiàn)出處
Article From 中國(guó)科學(xué)院上海冶金研究所; 材料物理與化學(xué)(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 電磁鑄造; 頻率; 4045鋁硅合金; 微觀組織;

Keywords Electromagnetic Casting;Frequency;4045 Al-Si Alloy;Microstructure;

低頻電磁鑄造7050鋁合金的組織與性能
高溫合金真空電磁鑄造補(bǔ)縮數(shù)學(xué)模型的建立與應(yīng)用
高溫合金母合金錠的真空電磁鑄造技術(shù)研究
低頻電磁鑄造對(duì)7050鋁合金羽毛晶組織缺陷的影響
熱處理對(duì)低頻電磁鑄造2024鋁合金力學(xué)性能的影響
均勻化處理對(duì)低頻電磁鑄造7050鋁合金微觀組織的影響
低過(guò)熱度電磁鑄造合金組織與性能
低頻電磁鑄造AZ41鎂合金的熱壓縮流變與組織
電磁鑄造對(duì)鋁合金鑄件力學(xué)性能的影響
電磁鑄造法制備的(Al_2O_3+Al_3Zr)_p/A359復(fù)合材料的磨損行為

  本文關(guān)鍵詞：電磁場(chǎng)頻率對(duì)電磁鑄造4045合金微觀組織的影響，由筆耕文化傳播整理發(fā)布。