本文選題：鋁合金 + 稀土�。� 參考：《中國稀土學(xué)報》2017年04期

【摘要】：將微量Ce添加到7085鋁合金中,采用金相分析、硬度測試、力學(xué)性能拉伸、斷口掃描、能譜分析等手段,研究了添加Ce后對7085鋁合金鑄態(tài)組織及力學(xué)性能的影響。結(jié)果表明:添加Ce后,Ce元素在固液界面前沿富集,出現(xiàn)成分過冷,使二次枝晶間距縮小,細(xì)化鑄態(tài)結(jié)晶組織;Ce的添加,Zn和Mg元素在晶界偏聚情況不再明顯,由晶界向基體轉(zhuǎn)移,使基體中合金元素增多,造成畸變能和應(yīng)變能增加,為彌散相析出提供了能量條件;添加Ce后,合金抗拉強度變化不大,塑性明顯提高,提高了7085鋁合金的綜合性能。
[Abstract]:The effect of ce addition on the as-cast microstructure and mechanical properties of 7085 aluminum alloy was studied by means of metallographic analysis, hardness test, tensile strength, fracture scanning and energy spectrum analysis. The results show that after the addition of ce, the element of ce is enriched at the front of solid-liquid interface, the composition is supercooled, the secondary dendrite spacing is reduced, and the addition of Zn and mg elements to refine the as-cast crystal structure is no longer obvious at the grain boundary, but is transferred from the grain boundary to the matrix. With the addition of ce, the tensile strength of the alloy increases little and the plasticity of the alloy increases obviously, and the comprehensive properties of 7085 aluminum alloy are improved.
【作者單位】： 煙臺南山學(xué)院工學(xué)院材料系;山東南山鋁業(yè)股份有限公司國家鋁合金壓力加工工程技術(shù)研究中心;
【基金】：山東省科技發(fā)展計劃項目(2014GGX102006) 山東省高等學(xué)校科研計劃項目(J16LA56) 山東省高等學(xué)校優(yōu)勢學(xué)科人才團隊培育計劃資助
【分類號】：TG146.21

【相似文獻】

相關(guān)期刊論文 前10條

1 ;力學(xué)性能二級人員取證復(fù)習(xí)參考題(之一)解答[J];理化檢驗(物理分冊);1997年12期

2 ;力學(xué)性能二級人員取證復(fù)習(xí)參考題(之三)解答[J];理化檢驗(物理分冊);1998年04期

3 陳金寶;高溫力學(xué)性能二級人員取證復(fù)習(xí)參考題(持久部分之五)解答[J];理化檢驗(物理分冊);2000年02期

4 潘葉金;電弧熔鑄的Nb-18Si-5Mo-5Hf-2C復(fù)合材料的力學(xué)性能[J];中國鉬業(yè);2003年03期

5 張美忠,李賀軍,李克智;三維編織復(fù)合材料的力學(xué)性能研究現(xiàn)狀[J];材料工程;2004年02期

6 游宇,周新貴;三維編織復(fù)合材料的力學(xué)性能[J];纖維復(fù)合材料;2004年04期

7 羅文波;唐欣;譚江華;趙榮國;;流變材料長期力學(xué)性能加速表征的若干進展[J];材料導(dǎo)報;2007年07期

8 嚴(yán)振宇;徐強;朱時珍;劉穎;;Sm_2Zr_2O_7-ZrB_2/SiC復(fù)合材料的制備及力學(xué)性能研究[J];稀有金屬材料與工程;2011年S1期

9 瞿欣;孫汝n，

本文編號：2087701