本文選題：Ti-鈦合金 + 組織均勻性��； 參考：《稀有金屬材料與工程》2017年03期

【摘要】：采用高周拉壓疲勞試驗(yàn),測(cè)試了片層Ti-55531合金的室溫高周疲勞性能。利用TEM、SEM等分析檢測(cè)方法,研究了近裂紋源區(qū)次生裂紋特征,以及顯微組織均勻性對(duì)高周疲勞裂紋萌生的影響。結(jié)果發(fā)現(xiàn):該片狀Ti-55531合金室溫高周疲勞強(qiáng)度σ_(-1)(1×10~7)可達(dá)639 MPa。合金顯微組織中含少量晶界α和大量10~50μm大小的組織不均勻區(qū),疲勞變形時(shí),晶界α處開(kāi)裂或組織不均勻區(qū)內(nèi)次生αs斷裂、α_s/β_r界面處開(kāi)裂等萌生微裂紋,促進(jìn)合金的疲勞失效。
[Abstract]:The high cycle fatigue properties of lamellar Ti-55531 alloy at room temperature were tested by high cycle tensile compression fatigue test. The characteristics of secondary crack near crack source and the effect of microstructure uniformity on the initiation of high cycle fatigue crack were studied by means of TEM SEM and other analytical methods. The results show that the high cycle fatigue strength 蟽 _ (-1) (1 脳 10 ~ (7) of the sheet Ti-55531 alloy at room temperature can reach 639 MPA. The microstructure of the alloy contains a small amount of grain boundary 偽 and a large amount of 1050 渭 m inhomogeneous microstructure. During fatigue deformation, the crack at the grain boundary 偽 or the secondary 偽 s fracture in the inhomogeneous region of the grain boundary, the crack at the interface of 偽 s / 尾 -r, and so on, promote the fatigue failure of the alloy.
【作者單位】： 西北工業(yè)大學(xué)凝固技術(shù)國(guó)家重點(diǎn)實(shí)驗(yàn)室;西北有色金屬研究院;
【基金】：國(guó)家自然科學(xué)基金項(xiàng)目(51471136) 國(guó)家國(guó)際科技合作(中法合作)項(xiàng)目(2015DFA1430)
【分類(lèi)號(hào)】：TG146.23

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 馬雷;;緩沖器的強(qiáng)度校核應(yīng)考慮高周疲勞[J];化工設(shè)計(jì)通訊;1990年02期

2 朱曉陽(yáng);奚建法;;低碳鋼在高周疲勞循環(huán)下的循環(huán)硬化問(wèn)題研究[J];機(jī)械強(qiáng)度;1991年02期

3 蔡俊鴻;;探討延長(zhǎng)高周疲勞零件壽命的某些途徑[J];四川冶金;1993年03期

4 關(guān)昕;孟延軍;;超高周疲勞的研究進(jìn)展[J];鋼鐵研究;2009年01期

5 張海威;何宇廷;程禮;高潮;張騰;;鈦合金超高周疲勞性能試驗(yàn)研究[J];航空材料學(xué)報(bào);2013年03期

6 鄧瑛;韓秀全;邵杰;鄧武警;;鈦合金三層空心結(jié)構(gòu)模擬件設(shè)計(jì)及高周疲勞實(shí)驗(yàn)[J];航空制造技術(shù);2013年16期

7 王紅衛(wèi)，楊大智，陳，

本文編號(hào)：2087127