本文選題：CrMoR鋼 + 析出物　； 參考：《金屬熱處理》2017年01期

【摘要】：通過(guò)SEM、XRD研究了回火及焊后熱處理對(duì)14Cr1MoR壓力容器鋼析出產(chǎn)物的微觀組織及其形貌的影響。結(jié)果表明:14Cr1MoR鋼中的析出相為Cr7C3碳化物,經(jīng)長(zhǎng)時(shí)間回火處理后主要在晶界附近長(zhǎng)大;模焊態(tài)中析出相的尺寸較回火態(tài)大,并趨于球化,衍射強(qiáng)度也明顯高于回火態(tài)。
[Abstract]:The effect of tempering and post-welding heat treatment on the microstructure and morphology of precipitated products of 14Cr1MoR pressure vessel steel was studied by means of SEMG-XRD. The results show that the precipitated phase is Cr _ 7C _ 3 carbides and mainly grows near grain boundary after long tempering, and the size of precipitated phase in die welding is larger than that of tempering state and tends to spheroidization, and the diffraction intensity is obviously higher than that of tempering state.
【作者單位】： 河鋼集團(tuán)鋼研總院;
【分類號(hào)】：TG142.1;TG161

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 唐國(guó)翌;鄭煬曾;朱靜;蔡其鞏;;09MnVTiN鋼板坯與板卷中析出物特征的研究[J];鋼鐵;1990年01期

2 盧鳳喜;;電工鋼中的析出物[J];武鋼技術(shù);2009年02期

3 張明德;1Cr18Ni9Ti不銹鋼中析出物相分析[J];特鋼技術(shù);1994年03期

4 王鳳玲，邵曉芬，，史淑君;從油脂脫膠析出物中分離提純磷脂[J];農(nóng)牧產(chǎn)品開(kāi)發(fā);1995年06期

5 李娜;項(xiàng)利;仇圣桃;趙沛;;高效電機(jī)用冷軋無(wú)取向電工鋼退火板析出物的析出特征研究[J];熱加工工藝;2013年24期

6 趙小平;龐兆夫;溫蘭伶;;含鈦低合金鋼中析出物固溶析出規(guī)律及長(zhǎng)大趨勢(shì)的研究[J];鞍鋼技術(shù);1987年04期

7 賀秀麗;宋銳;于波;邱延華;王波;;高強(qiáng)度容器試驗(yàn)鋼析出物的試驗(yàn)研究[J];山東冶金;2007年S2期

8 魏緒儉，申秀清，劉伶;不銹鋼中析出物標(biāo)準(zhǔn)樣品的研制[J];冶金分析;1994年04期

9 袁曉敏,張慶安,孫全社;搪瓷鋼板中析出物的測(cè)定[J];鋼鐵研究學(xué)報(bào);2000年05期

10 王明林;成國(guó)光;仇圣桃;趙沛;干勇;;凝固過(guò)程中含鈦析出物的析出行為[J];鋼鐵研究學(xué)報(bào);2007年05期

相關(guān)會(huì)議論文 前5條

1 趙紅陽(yáng);王項(xiàng)龍;劉源;;冷軋無(wú)取向硅鋼中的析出物分析[A];2010第11屆中國(guó)電工鋼專業(yè)學(xué)術(shù)年會(huì)論文集[C];2010年

2 侯華興;王道遠(yuǎn);張鵬遠(yuǎn);張濤;張萬(wàn)山;沙孝春;魯強(qiáng);孫群;;超低碳貝氏體鋼連鑄坯組織特征及其析出物形態(tài)在熱加工過(guò)程中的演變[A];中國(guó)金屬學(xué)會(huì)2003中國(guó)鋼鐵年會(huì)論文集（4）[C];2003年

3 項(xiàng)利;岳爾斌;李建軍;;主要工藝對(duì)CSP流程生產(chǎn)低碳低硅無(wú)取向硅鋼組織、析出物和磁性能的影響[A];2010第11屆中國(guó)電工鋼專業(yè)學(xué)術(shù)年會(huì)論文集[C];2010年

4 楊海林;周一中;黃為民;馬珩v

本文編號(hào)：2056725