本文選題：光纖激光焊接 + A鋁鋰合金　； 參考：《機(jī)械工程學(xué)報(bào)》2017年16期

【摘要】：基于紅外熱像測量技術(shù),通過對(duì)不同保護(hù)氣體時(shí),光纖激光焊接5A90鋁鋰合金過程的溫度場研究,獲得了如下結(jié)論:改變焊接速度的對(duì)比試驗(yàn)表明,保護(hù)氣體對(duì)光纖激光焊接5A90溫度場特征及其演變規(guī)律影響很大,且在不同焊接速度下,其影響規(guī)律也略有不同,但是總體而言,氦氣作為保護(hù)氣體,會(huì)使得小孔與熔池更加趨于穩(wěn)定,小孔中心及小孔后端溫度更低。改變激光功率的對(duì)比試驗(yàn)表明,氦氣保護(hù)時(shí),對(duì)正面焊縫溫度場分布幾乎無影響,但是在氬氣保護(hù)時(shí),影響卻較大,其小孔中心特征值溫度均值增加158℃,熔池長度的差異也很大。結(jié)果表明,這兩種保護(hù)氣體下激光能量的吸收、熔池的流動(dòng)等有所不同,也表明改變激光功率和改變焊接速度,即使熱輸入相同,但是焊縫的熱歷程卻有所不同。
[Abstract]:Based on the infrared thermal image measurement technology, the following conclusion is obtained through the study of the temperature field of 5A90 Al Li alloy by optical fiber laser welding with different protective gases. The following conclusion is obtained: the contrast test of the change of welding speed shows that the protective gas has a great influence on the temperature field characteristics and the variation law of the 5A90 welding of the fiber laser welding, and at different welding speed, it has a great influence on the temperature field of the optical fiber laser welding. The influence rules are also slightly different, but in general, the helium gas as a protective gas will make the hole and pool more stable, the center of the hole and the back end of the hole are lower. The contrast test of the laser power shows that the temperature field distribution of the weld seam is almost no influence when the helium gas protection is protected, but the effect is larger when the argon gas is protected. The mean value of the central characteristic temperature of the small holes is increased by 158 degrees C, and the difference in the length of the molten pool is also great. The results show that the absorption of laser energy and the flow of the molten pool under the two kinds of protective gases are different, and it also shows that the laser power and the welding speed are changed, even the heat input is the same, but the heat course of the weld is different.
【作者單位】： 北京航空制造工程研究所高能束流加工技術(shù)重點(diǎn)實(shí)驗(yàn)室;
【分類號(hào)】：TG456.7

【相似文獻(xiàn)】

相關(guān)期刊論文 前2條

1 劉穎韜;郭興旺;郭廣平;;紅外熱像檢測的3D建模與1D建模的對(duì)比[J];無損檢測;2011年02期

2 李托雅;田裕鵬;王平;孫冉;;感應(yīng)激勵(lì)紅外熱像無損檢測及其在裂紋檢測中的應(yīng)用[J];無損檢測;2014年01期

相關(guān)博士學(xué)位論文 前1條

1 閆志峰;基于紅外熱像法鎂合金及其焊接接頭疲勞行為及評(píng)定理論研究[D];太原理工大學(xué);2014年

相關(guān)碩士學(xué)位論文 前7條

1 杜鵬;承壓設(shè)備紅外熱像無損檢測技術(shù)的研究[D];福州大學(xué);2013年

2 李贊;金屬結(jié)構(gòu)件裂紋超聲紅外熱像檢測及其激勵(lì)參數(shù)影響規(guī)律研究[D];湖南科技大學(xué);2016年

3 侯培軍;基于定量紅外熱像法的鈦合金疲勞性能分析[D];大連理工大學(xué);2014年

4 李托雅;感應(yīng)激勵(lì)紅外熱像無損檢測技術(shù)研究[D];南京航空航天大學(xué);2013年

5 王凱;基于紅外熱像法的金屬高周疲勞性能研究[D];太原理工大學(xué);2013年

6 張虔銘;基于紅外熱像法的AZ31B鎂合金應(yīng)力集中系數(shù)研究[D];太原理工大學(xué);2015年

7 楊宏偉;紅外熱像法表征AZ31B鎂合金電子束焊接接頭疲勞行為及斷裂機(jī)理的研究[D];太原理工大學(xué);2015年

，

本文編號(hào)：2051391