文獻名稱：低頻電磁鑄造超高強高韌鋁合金元素晶內固溶度和力學性能研究

    前言：采用電磁細晶鑄造技術,降低其頻率,半連續(xù)鑄造一種新的超高強高韌鋁合金(10Zn-2.5Mg-2.5Cu-0.15Zr-余量Al),考察了低頻電磁鑄造與常規(guī)DC鑄造組織、元素晶內固溶度和力學性能的區(qū)別,重點考察了電磁場頻率和安匝數(shù)對鑄錠元素晶內固溶度和力學性能的影響規(guī)律。結果表明,相對常規(guī)DC鑄造,低頻電磁鑄造組織細小均勻等軸,合金元素Zn,Mg和Cu在晶內的固溶度增加,鑄態(tài)維氏硬度、延伸率和拉伸強度增加。頻率為15～25Hz和安匝數(shù)12800～16000AT時,合金元素Zn,Mg和Cu在晶內的固溶度最高,錠坯維氏硬度、延伸率和拉伸強度最大。其12mm的擠壓棒材熱處理后的拉伸強度極限為780MPa,延伸率大于8%。
    A new superhigh strength and toughness Al alloy (10Zn25Mg25Cu015ZrbalanceAl) was semicontinuously cast on the basis of CREM (casting, refining, electromagnetic), by lowering the electromagnetic frequency to 15～35Hz The differences of microstructure, intracrytalline element solubility and mechanical properties between DC and low frequency electromagnetic casting were investigated The effect of electromagnetic frequency and number of ampere turns on intracrytalline element solubility and mechanical...

文獻名稱 低頻電磁鑄造超高強高韌鋁合金元素晶內固溶度和力學性能研究

Article Name
英文(英語)翻譯 Intracrytalline element solubility and mechanical property of a new super-high strength and toughness Al alloy cast under low frequency electromagnetic field;

作者 董杰; 崔建忠; 趙志浩;

Author DONG Jie;CUI Jianzhong;ZHAO Zhihaotion;Northeastern University;Shenyang 110004;China）;

作者單位
Author Agencies 東北大學材料電磁過程研究教育部重點實驗室; 東北大學材料電磁過程研究教育部重點實驗室 遼寧沈陽; 110004; 遼寧沈陽;

文獻出處
Article From 中國科學院上海冶金研究所; 材料物理與化學(專業(yè)) 博士論文 2000年度

關鍵詞 低頻; 電磁鑄造; 固溶度; 力學性能; Al-Zn-Mg-Cu-Zr;

Keywords low frequency;electromagnetic casting;solubility;mechanical property;Al-Zn-Mg-Cu-Zr;

天然超低頻電磁場日夜交替及其穩(wěn)定性分析
低頻環(huán)境噪聲對思維判斷能力的干擾影響
低頻電磁鑄造7050鋁合金的組織與性能
基于AT89S51單片機的低頻振動攻絲微機控制系統(tǒng)設計
甚低頻電磁法在礦體勘查中的應用
低頻方波高強度氣體放電燈電子鎮(zhèn)流器
甚低頻電磁法在草原覆蓋區(qū)礦產勘查中的應用
低頻振動切削對加工表面影響的機理研究
淺析礦井交流提升低頻相控系統(tǒng)的改造
鉆井模擬中測井信號去噪及低頻信息提取技術研究

  本文關鍵詞：低頻電磁鑄造超高強高韌鋁合金元素晶內固溶度和力學性能研究，由筆耕文化傳播整理發(fā)布。