本文選題：高速鋼車刀 + 激光熔覆�。� 參考：《寧波大學(xué)》2017年碩士論文

【摘要】：車削加工中,連續(xù)不斷的切屑會影響工件表面質(zhì)量,減少刀具壽命,危及到操作人員的安全。本文應(yīng)用激光熔覆技術(shù)在高速鋼車刀的前刀面上制作出無裂紋、氣孔缺陷的凸包形斷屑臺,研究其制作工藝和方法。首先,通過車削LY12硬鋁合金實驗證明激光熔覆斷屑臺高速鋼車刀斷屑效果優(yōu)于普通高速鋼車刀,能夠獲得較高的加工表面質(zhì)量,但是熔覆斷屑臺截面有裂紋、氣孔、冶金結(jié)合不良等缺陷。通過析因?qū)嶒炘O(shè)計的方法,研究激光工藝參數(shù)對熔覆裂紋缺陷的影響,建立了裂紋率與工藝參數(shù)之間的回歸方程。研究表明,熔覆工藝參數(shù)對裂紋的影響程度依次為電流、脈寬、頻率、掃描速度、離焦量,此外,熔覆裂紋的產(chǎn)生還受到工藝參數(shù)間交互作用的影響。然后,通過對幾種熔覆粉末的激光熔覆實驗,確定出適于W6Mo5Cr4V2刀具材料的熔覆粉末材料,即利用混入質(zhì)量分?jǐn)?shù)為15%WC-12Co的M2高速鋼粉末激光熔覆制作的斷屑臺其顯微硬度較高,熔覆截面無裂紋、氣孔等缺陷,并通過熱膨脹系數(shù)、XRD物相、硬度分析、金相組織分析等手段來解釋說明熔覆裂紋消除的原因。最后,通過單因素實驗方法研究了激光工藝參數(shù)對熔覆凸包幾何尺寸的影響規(guī)律,并且利用正交實驗的方法對熔覆凸包的激光工藝參數(shù)進(jìn)行了優(yōu)化。
[Abstract]:During turning, the continuous chip will affect the surface quality of the workpiece, reduce the tool life and endanger the safety of the operator. In this paper, the laser cladding technique is used to fabricate the convex cladding chip table without crack and pore defect on the front face of high speed steel turning tool, and the fabrication technology and method are studied. Firstly, the experiment of turning LY12 hard aluminum alloy shows that the chip breaking effect of high speed steel turning tool of laser cladding chip table is better than that of ordinary high speed steel turning tool, and the surface quality of machined surface can be obtained, but there are cracks and pores in the cross section of cladding chip table. Defects such as poor metallurgical bonding. The effect of laser process parameters on cladding crack defects was studied by factorial experiment. The regression equation between crack rate and process parameters was established. The results show that the influence of cladding process parameters on the crack is in order of current pulse width frequency scanning speed and defocus. In addition the process parameters also influence the production of the cladding crack. Then, through the laser cladding experiment of several kinds of cladding powder, the cladding powder material suitable for W6Mo5Cr4V2 tool material is determined, that is, the microhardness of the chip breaking table made of M2 high speed steel powder cladding with mixed mass fraction of 15%WC-12Co is high. The cladding section has no defects such as cracks, pores, and so on. The reasons for the elimination of cladding cracks are explained by means of thermal expansion coefficient XRD, hardness analysis and metallographic structure analysis. Finally, the influence of laser parameters on the geometrical size of cladding convex hull is studied by single factor experiment, and the laser technological parameters of cladding convex hull are optimized by orthogonal experiment.
【學(xué)位授予單位】：寧波大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：TG174.4;TG712

【參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 鄒磊;武穎;岑啟宏;;電脈沖處理對W6Mo5Cr4V2高速鋼的影響[J];材料工程;2016年02期

2 李美艷;蔡春波;韓彬;王勇;;預(yù)熱對激光熔覆陶瓷涂層溫度場和應(yīng)力場影響[J];材料熱處理學(xué)報;2015年12期

3 李闖;劉洪喜;張曉偉;陶喜德;蔣業(yè)華;;40Cr刀具鋼表面激光熔覆鈷基碳化物復(fù)合涂層的組織與性能[J];中國激光;2015年11期

4 戴德平;蔣小華;蔡建鵬;蘆鳳桂;陳源;李鑄國;鄧德安;;激光熔覆Inconel718鎳基合金溫度場與應(yīng)力場模擬[J];中國激光;2015年09期

5 付福興;暢庚榕;趙小俠;張艷麗;;激光光斑直徑對熔覆層裂紋的影響[J];激光與光電子學(xué)進(jìn)展;2015年03期

6 張艷梅;華海;帥歌國;揭曉華;曾鵬;;激光熔覆微納米WC顆粒增強(qiáng)鎳基金屬陶瓷涂層的裂紋研究[J];熱加工工藝;2014年24期

7 鄭子云;馬冰;馮勝強(qiáng);劉光;;工藝參數(shù)對蠕墨鑄鐵激光熔凝淬火帶裂紋率和形貌的影響[J];焊接學(xué)報;2014年04期

8 張毅斌;熊征;童法松;;脈沖CO_2激光熔覆K403合金層工藝研究[J];材料開發(fā)與應(yīng)用;2013年05期

9 吳東江;楊策;吳楠;郭玉泉;馬廣義;郭東明;;SiC顆粒摻雜對激光直接成形Al_2O_3陶瓷裂紋敏感性的影響[J];光學(xué)精密工程;2012年07期

10 王東生;田宗軍;王涇文;段宗銀;沈理達(dá);黃因慧;;一種通過改變激光功率密度分布控制熔覆層裂紋的方法[J];中國激光;2011年01期

相關(guān)博士學(xué)位論文 前1條

1 毛懷東;激光熔覆層裂紋控制方法與實踐[D];天津大學(xué);2007年

相關(guān)碩士學(xué)位論文 前4條

1 鄭小宇;激光熔覆Ni20Cr復(fù)合涂層的微觀組織和摩擦磨損性能[D];燕山大學(xué);2015年

2 白梅;Q235鋼表面激光熔覆316L涂層及316L/Al_2O_3復(fù)合涂層研究[D];中北大學(xué);2015年

3 苗國策;等離子噴焊Ni基WC增強(qiáng)耐磨涂層的研究[D];哈爾濱工業(yè)大學(xué);2013年

4 陳川川;工藝參數(shù)對激光熔覆層影響的研究[D];湖南大學(xué);2013年

，

本文編號：1981271